Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 376 Polyester Film Melinex® 376 is a translucent, smooth, matte polyester film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 378 Polyester Film Melinex® 378 is a translucent, matte, polyester film which has a rougher surface (lower surface gloss) than Melinex® 377.Approvals: UL Recognition - Product has been registered with Underwriters L.. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® WCW Polyester Film, 200 Gauge Melinex® WCW is a translucent white polyester film with a rough surface for superior handling characteristics.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® WCW Polyester Film, 75 Gauge Melinex® WCW is a translucent white polyester film with a rough surface for superior handling characteristics.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® WCW Polyester Film, 92 Gauge Melinex® WCW is a translucent white polyester film with a rough surface for superior handling characteristics.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EL Polyester Film, 300 Gauge Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab.. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC11/WC22 Polyester Film, 300 Gauge Mylar® type WC11 films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectric and good handlin.. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 535 Polyester Film Melinex® 535 is a high clarity polyester film that is two-side pretreated to promote adhesion to aqueous based coatings.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 623 Polyester Film, 500 Gauge Melinex® 623 is a super clear polyester film pretreated on both surfaces to give superior solvent adhesion and improved handleability.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 680 Polyester Film, 500 Gauge Melinex® 680 is a super clear polyester film, pretreated on one side to promote adhesion with improved handleability. It is high clarity, non-yellow base with excellent adhesion on the pretreated s.. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Mylar® A Polyester Film, 300 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, .. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Mylar® MDA Polyester Film, 300 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion.. |
|||
Film Tensile Strength at Break, TD | 214 MPa | 31000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC Polyester Film, 300 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char.. |