Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
Polimeri Europa Clearflex® CL 508 Octene Copolymer Linear Medium Density Polyethylene Clearflex CL 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 508 exhibit a good bal.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
SABIC 118 Series Linear Low Density Polyethylene for Blown Film Product Description: 118 series resins are Linear Low Density Polyethylene grades suitable for general purpose packaging. Films produced using these resins yield good tensile properties, impact st.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
SABIC 120W Linear Low Density Polyethylene for Blown Film Product Description: 120W is a Linear Low Density Polyethylene grade suitable for general purpose packaging. Films produced using this resin yield good tensile properties, impact strength and opti.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
Polimeri Europa Greenflex® FC 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FC 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FC 45 exhibit good optical properties, excellent impact resistance and low creep.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® ABS 1410 PRE-ELEC ABS 1410 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ABS 141.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Reliance Industries Reclair F18010 Polyethylene Butene comonomer based Linear Low Density Polyethylene blow film grade. Applications:lamination films. Information provided by Reliance Industries |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
Polimeri Europa Greenflex® FD 50 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FD 50 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FD 50 exhibit good optical and sealing properties, high flexibility and toughnes.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
SABIC HP0322N Low Density Polyethylene for Blown Film Product Description: HP0322N is a Low Density Polyethylene grade suitable for producing heavy duty films and contains no slip or antiblock additives. It yields outstanding toughness and optical pr.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
NOVA Chemicals Sclair® 14K1 Octene LMDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882-02 |
Ipiranga Petrochem LB 0216 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Iran Petrochemical (PCC) LL22501 Linear Low Density Polyethylene 22501 is a high stiffness LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels a.. |
|||
Film Tensile Strength at Break, TD | 30.0 - 45.0 MPa | 4350 - 6530 psi | 50% RH; DIN 53455 |
Stanelco Bioplast® GS 2189 Biodegradable Plastic Bioplast 2189 is a product that is optimised for sheet extrusion, injection and compression moulding. It is always biodegradable and readily compostable in thin sections, this material is useable i.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
SCG Chemicals EL-Leneâ„¢ H5604F High Density Polyethylene Film Key Characteristics:High tensile strengthHigh dart impactHigh stiffnessLow gel contentGood moisture barrierRecommended Applications: Films for shopping bag, T-shirt bag, garbage bag, liner bagInfor.. |
|||
Film Tensile Strength at Break, TD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis BB213CF Polypropylene Copolymer BB213CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BB213CF is recommended for food packaging.. |
|||
Film Tensile Strength at Break, TD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis BD212CF Polypropylene Copolymer BD212CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BD212CF is designed for food packaging, l.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
Borealis Borclear™ RE936CF Polypropylene Random Copolymer Borclear™ RE936CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: food packaging, lamination films, and stationary fil.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
Borealis Bormed™ RE806CF Polypropylene Random Copolymer Bormed™ RE806CF is a random copolymer. The material is specially formulated for medical applications. Applications: Bormed™ RE806CF is recommended for medical packaging. Bormed™ RE806CF contai.. |
|||
Film Tensile Strength at Break, TD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis Bormod™ HD905CF Polypropylene Homopolymer for Cast Film Bormod HD905CF is a high crystallinity homopolymer film resin, based on special Borstar nucleating technology, suitable for the manufacturing of unoriented film on chill roll process. It is recomme.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | 50 µm (2 mil) film; ASTM D882 |
DuPont Nucrel® 31001 Ethylene-Acrylic Acid Copolymer Resin for Blown and Cast Film 9.5 wt% Acrylic Acid.Nucrel® 31001 is an ethylene-acrylic acid copolymer resin available for use in blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins.F.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | Cast Film at 1 mil; ASTM D-882 |
Chevron Phillips MarFlex® 7114 Polyethylene; LLDPE Hexene linear low density polyethylene. This LLDPE is tailored for applications that require: Good stiffness at thin gaugesGood drawdownExcellent processabilityCan use straight or in blends with L.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem FG31 LLDPE Blown Film Extrusion Polyethylene Copolymer FG31 is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process. It was developed for blown film extrusion in blends with polyethylene. Films obtained with this pr.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem Green PE SLL218/21 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Line.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem LH 218 LLDPE Cast Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Stretch film; shrink film; "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem LL118/21 Blown Film Extrusion Linear Low Density Polyethylene Description: LL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties a.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem LL218/21 Cast Film Extrusion Linear Low Density Polyethylene Liners, LDPE and HDPE blends; General use packages; Technical films for automatic packaging.Additives: Antiblock, DInformation provided by Braskem. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LL318 LLDPE Cast Film Extrusion Polyethylene Copolymer LL318 is a linear low-density polyethylene, copolymer of butene-1, produced by the Spherilene process. It was developed for cast film extrusion. Films obtained with this product show good mechanical.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LL6802N LLDPE Blown Film Extrusion Polyethylene Copolymer LL6802N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid .. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
DuPont™ Surlyn® 2601 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 2601 is an ionomer resin available for use in blown and cast film operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene resins. Applicati.. |
|||
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
ExxonMobil Exceed™ 2018EB Blown Film Resin
(discontinued **) Exceed 2018EB resin is an ethylene based polymer produced with metallocene single site catalysts using ExxonMobil Chemicals Exxpol® Technology. The higher melt index makes this polymer ideally sui.. |