Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 60 CSR-2 OPP Film Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 75 SLP OPP Film Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminatin.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 60 SLP OPP Film Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminatin.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 19LL-101 OPP Film Product Description: A clear, one-side treated, polypropylene film that is designed to provide exceptional clarity and print protection when used as overlaminates in pressure-sensitive labeling appl.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 25LL-101 OPP Film Product Description: A clear, one-side treated, polypropylene film that is designed to provide exceptional clarity and print protection when used as overlaminates in pressure-sensitive labeling appl.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 30LL-101 OPP Film Product Description: A clear, one-side treated, polypropylene film that is designed to provide exceptional clarity and print protection when used as overlaminates in pressure-sensitive labeling appl.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 582 Polyester Film, 400 Gauge Melinex® 582 is a high clarity polyester film which is two-side hydrophilic pretreated to promote adhesion to many industrial aqueous coating and inks.Approvals: UL Recognition - Product has been r.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LBTW Polyester Film, 75 Gauge Mylar® LBTW is an uncoated, transparent polyester film that has been corona treated on one side to provide superior wetting and adhesion of inks, primers, and adhesives. Mylar® LBTW is commerciall.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB01 (formerly known as XM924) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and a polyvinylidene chlor.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the op.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® OB13AF Polyester Film, 150 Gauge Product Description: Mylar® OB13AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opposite s.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat seal.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® OL2 Polyester Film, 100 Gauge Product Description: Mylar® OL2 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sealable lidding film in packaging refrigerated and f.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RB42AF Polyester Film, 100 Gauge Product Description: Mylar® RB42AF is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer and polyvinylidene chloride (PVdC) layer on the opposite side. .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RB43 Polyester Film, 100 Gauge Mylar® RB43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opposite side. Mylar® R.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RB52 Polyester Film, 50 Gauge Product Description: Mylar® RB52 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opp.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL33 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL33 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ExxonMobil Method |
ExxonMobil Bicor® 110 ASB-X OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film designed for broad use in many applications, including overwrap, horizontal, and vertical packaging. ASB-X is good for heavy .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 120 CSR-2 OPP Film Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and .. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 516 Polyester Film Melinex® 516 is a high clarity polyester film which is pretreated on both sides for slip to combine good handling properties with high clarity and brilliance.Typical Applications: Some typical uses.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 516D Polyester Film A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brilliance.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the op.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 516R Polyester Film A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brillianceInformation provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® LBT-2 is an uncoated, transparent, exceptionally strong film used as a substrate for laminating and extrusion coating and as a component of packagi.. |
|||
Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 510 |
ExxonMobil Bicor® 120 LCX OPP Film One-side treated, one-side sealable OPP film designed for use in a lamination. It is typically laminated to Metallyte, HBS-2, SPW, and itself to create lap sealable packages. The high energy surfac.. |