Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 110 AXT OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film delivering an advanced level of moisture and oxygen battier protection. This film is designed for use in (unsupported and sur.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 120 AB-X OPP Film Product Description: Bicor AB-X is a two-side coated, sealable OPP film designed for general use in many applications, including overwrap, horizontal and vertical packaging. This film is suitable as.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 420 HS OPP Film Product Description: Bicor HS is a two-side coated, sealable OPP film designed for general use in overwrap and horizontal packaging. This film is suitable as an unsupported web or lamination. It can.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 313 Polyester Film Melinex® 313 is a general purpose polyester film with consistently good handling properties. It is pretreated on one side for adhesion.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 505 Polyester Film Melinex® 505 is a high clarity polyester film which is pretreated on both sides to promote adhesion to most industrial coating and inks.Approvals: UL 94 VTM-2 - for 1000 gauge (0.26mm) onlyInformat.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® CL Polyester Film, 50 Gauge Mylar® CL is an exceptionally strong polyester film designed to package foods. Foods can be heated or cooked in this film at temperatures up to 400°F. Mylar® CL is commercially available in nomin.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EC Polyester Film, 200 Gauge Mylar® EC films are electrical grade films designed for use in applications where improved dimensional stability is required. In addition to lower levels of shrinkage, Mylar® EC films offer outsta.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33100 psi | ASTM D882 |
DuPont Teijin Films Mylar® M34 Polyester Film, 50 Gauge (13 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, solvent coated on one side with a PVDC copolymer. The coating is heat sealable, and is an excellent moisture and o.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 200 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 48 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 500 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 60 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 92 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33100 psi | ASTM D882 |
DuPont Teijin Films Mylar® MC2 Polyester Film, 100 Gauge (25 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A polyester film with a vacuum deposited layer of aluminum on one side and overcoated on both sides with a heat sealable PVDC copolymer. The film has exce.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 105 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 140 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 175 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 300 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 400 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 48 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 92 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 120 LTSC OPP Film Product Description: Bicor LTSC is a two-side coated OPP film which is designed for use in high-speed or demanding horizontal, fin seal, packaging applications. The low-temperature seal coating (LTS.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® D804 Polyester Film, 60 Gauge Mylar® D804 is a super clear, biaxially oriented, co-extruded polyester film, available in 60, 75 and 92 gauge. Mylar® D804 is two-side pretreated for printing and adhesive lamination. Approvals: .. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 300 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® M461 Polyester Film, 400 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX Polyester Film, 200 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33100 psi | ASTM D882 |
DuPont Teijin Films Mylar® M30 Polyester Film, 50 Gauge (14 µm), PVDC Coated
(discontinued **) Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, solvent coated on both sides with a PVDC copolymer. The coating is heat sealable, and is an excellent moisture and.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33100 psi | ASTM D882 |
DuPont Teijin Films Mylar® M30 Polyester Film, 75 Gauge (21 µm), PVDC Coated
(discontinued **) Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, solvent coated on both sides with a PVDC copolymer. The coating is heat sealable, and is an excellent moisture and.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33100 psi | ASTM D882 |
DuPont Teijin Films Mylar® 50 M44E Polyester Film, One-Sided PVDC Barrier Coated, 50 Gauge
(discontinued **)& Data provided by DuPont Packaging Polymers.A transparent, exceptionally strong polyester film, coated on one side with an oxygen and moisture barrier PVDC copolymer. It is used as a substrate in co.. |
|||
Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
DuPont Teijin Films Mylar® MDA Polyester Film, 200 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion.. |