Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® CP 1317 PRE-ELEC CP 1317 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1317 .. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® CP 1319 PRE-ELEC CP 1319 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1319 .. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
SABIC HP4023W Low Density Polyethylene for Blown Film Product Description: HP4023W is a Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It yields excellent processability with goo.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
ExxonMobil Escorene® LD-102 LDPE Drawdown Resin, 0.5 mil Film
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer, good clarity, laundry and dry cleaning film resin capable of providing a tough film in very thin gauges.Applications: Dry cleaning es.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
ExxonMobil Escorene® LD-336 EVA Film Resin, Clarity, Very High Drawdown
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.5% vinyl acetate copolymer blown film resin capable of very high drawdown with excellent clarity.Applications: Very thin heat seal layers; Light.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO R527-1 |
Iran Petrochemical (PCC) 2004TC37 Low Density Polyethylene LDPE 2004TC37: Light duty film used for very thin films requiring good optical properties for general packaging.Information provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
SCG Chemicals EL-Leneâ„¢ LD1905F Low Density Polyethylene Film Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE, LLDPEContains 1500 ppm slip agent and 2600 ppm antiblocking agentRecommended Applications:General purpose bagVeg.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
SCG Chemicals EL-Leneâ„¢ LD1905FA Low Density Polyethylene Film Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE and LDPE to improve tear resistance and seal strengthContains 1000 ppm slip agent and 700 ppm antiblocking agentR.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 527-3 |
Borealis Himod™ FT7324 . LDPE for Film Himod FT7324 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | 500 mm/min; ISO 527-3 |
DuPont Elvaloy® 3217 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3217 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3217 AC has been developed for film applications requiring a combination of softness, toughness and low friction. Typi.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 1184 |
Carmel Olefins IPETHENE® 320 Low Density Polyethylene IPETHENE® 320 is a general purpose low density polyethylene film extrusion grade, containing no additives. It exhibits good mechanical and optical properties. APPLICATIONS IPETHENE® 320 is mainl.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 1184 |
Carmel Olefins IPETHENE® 322 Low Density Polyethylene IPETHENE® 322 is a general purpose low density polyethylene film extrusion grade. It contains a medium level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between .. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 1184 |
Carmel Olefins IPETHENE® 323 Low Density Polyethylene IPETHENE® 323 is a general purpose low density polyethylene film extrusion grade. It contains a high level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between me.. |
|||
Film Tensile Strength at Break, TD | >= 15.0 MPa | >= 2180 psi | ASTM D882 |
Huntsman Rexell® V8402 Cast Film Extrusion LLDPE
(discontinued **) Ultra linear-low density copolymer, blown film extrusion, FDA compliant.Features: Excellent mechanical strength, low sealing temperature, and good flex crack resistanceApplications: Sealing layer in.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
Huntsman PE1059 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down and good processability.Applications: Film extrusion: non-abrasive packaging applications.FDA Notes: Conforms to FDA regulation 21 CFR 177.. |
|||
Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
Huntsman PE1158 EVA Film Extrusion
(discontinued **) 1.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: .. |
|||
Film Tensile Strength at Break, TD | 15.0 - 18.0 MPa | 2180 - 2610 psi | Average value: 17.0 MPa Grade Count:3 |
Overview of materials for Ethylene Butyl Acrylate This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Butyl Acrylate". Each property range of values reported is minimum and maximum values of approp.. |