Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Fracture Toughness | 5.00 MPa-m½ | 4.55 ksi-in½ | ASTM C1421 |
M Cubed Technologies RBBC-751 Reaction Bonded Boron Carbide Reaction-bonded boron carbide for extreme wear environments. Can be cast into very large components (greater than 4 ft. square)Information provided by M Cubed Technologies, Inc. |
|||
Fracture Toughness | 5.00 - 6.00 MPa-m½ | 4.55 - 5.46 ksi-in½ | Notched Beam |
CoorsTek Alumina-Zirconia Composite, AZ-25 Information provided by CoorsTek. |
|||
Fracture Toughness | 5.00 - 6.00 MPa-m½ | 4.55 - 5.46 ksi-in½ | Notched Beam |
CoorsTek Zirconia-Toughened Alumina, ZTA Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Fracture Toughness | 5.00 MPa-m½ | 4.55 ksi-in½ | |
Astro Met AmAlOx 68 Alumina - Aluminum Oxide General Description:AmAlOx 68 alumina (Astro Met Aluminum Oxide) is a high purity 99.8% aluminum oxide (alumina) ceramic which has been developed and optimized for maximum wear resistance and corros.. |
|||
Fracture Toughness | 5.00 MPa-m½ | 4.55 ksi-in½ | SEVNB; ISO 23 146 |
CeramTec MZ BE Zirconia 3Y-TZP, Dental Grade MZ BE is a yttria-stabilized tetragonal zirconia used in dental applications. |
|||
Fracture Toughness | 5.00 MPa-m½ | 4.55 ksi-in½ | |
Ceradyne Ceralloy® 147-1E Silicon Nitride Ceralloy® 147 Hot Pressed Silicon Nitride (HPSN) can be formulated into a variety of compositions having minimal densification aids. These HPSN compositions offer the highest strength of Ceradynes .. |