Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 4.30 GPa | 624 ksi | |
Plastcom SLOVALEN PC 19 GF 20 PP, 20% glass fibre, mod. of mech. properties FeaturesModified copolymer PP for iextrusion, chemically reinforced with 20% glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP. Applied i.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | |
Plastcom SLOVALEN PC 79 GF 20 PP, 20% glass fibre, mod. of mech. prop. FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 20% glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® XCM840 PC+ABS High stiffness PC/ABS blend offering practical impact, low CTE, high heat resistance, with good aesthetics suitable for injection molding |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527-1/-2 |
Quadrant EPP Ketron® 1000 PEEK unfilled, extruded (ISO Data) Ketron PEEK-1000 stock shapes are produced from virgin polyetheretherketone resin and offer the highest toughness and impact strength of all Ketron PEEK grades. Both Ketron PEEK-1000 natural & black.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP FARADEX DX92079 PC (Europe-Africa-Middle East) LNP* Faradex* DX92079 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Bead, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding, Mold Release... |
|||
Tensile Modulus | 4.30 GPa @Temperature 175 °C |
624 ksi @Temperature 347 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | TD; ISO 527 |
Victrex® APTIV® 1102-050M Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline, 20% Mineral Filled APTIV PEEK 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance application.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min |
Polimeri Europa KOBLEND PCA PD 935 G2 PC+ABS, 10% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 10% glass fibres, high stiffness, very good dimensional stability. Vicat/B50 = 135°C Main application field.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527-1/-2 |
Lanxess Durethan® DP 1100/30 H2.0 901510 Nylon 6, Micro Glass Balls PA6, molding grade, micro glass balls, good heat-ageing resistance |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RBG16I PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RBG16I is a compound based on Nylon 66 resin containing Glass Bead, Graphite. Added features of this material include: High Impact. |
|||
Tensile Modulus | 4.30 GPa @Temperature 175 °C |
624 ksi @Temperature 347 °F |
4; ISO 527-2 |
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high .. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON PD000 PA 6 (Europe-Africa-Middle East) LNP* STAT-KON* PD000 is a compound based on PA 6 resin containing Carbon Powder. Added features include: Electrically Conductive. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X4870HH PC+PET (Asia Pacific) Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
Tensile Modulus | 4.30 GPa @Temperature 175 °C |
624 ksi @Temperature 347 °F |
4; ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X5630 PC+PET (Asia Pacific) Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RB004 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RB004 is a compound based on PA 66 resin containing Glass Beads.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527-1/-2 |
Unitika M1030DH PA6, Dry Nano composite nylonInformation provided by Unitika Ltd. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 GV 15 HWCP 15% Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 GV 5 HWCP 5% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ASTM D638 |
Ensinger Tecapeek® ID Metal Detectable Polyetheretherketone Tecapeek™ ID metal detectable polyetheretherketone, made from Victrex® PEEK 450G polymer, is formulated to reduce the risk of product contamination and allow for easy detection of fragments in the.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 50mm/min; ISO 527-1 |
Denka TE-10 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 50mm/min; ISO 527-1 |
Denka TP-803 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
Eurostar Staramide RB004 PA66, 20% Glass Bead Filled, Injection Molded Staramide RB004 is a 20% Glass Bead Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527-1/-2 |
DSM Akulon® K224-HG4 Nylon 6-20% Glass Reinforced (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527 |
Azdel Plus R300-B01 30% Continuous Random Fiber Mat / PP Resin Matrix AZDEL® R300-B01 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a polypropylene resin matrix. This composite material features high flow pr.. |
|||
Tensile Modulus | 4.30 GPa @Temperature 80.0 °C |
624 ksi @Temperature 176 °F |
ISO Data |
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also.. |
|||
Tensile Modulus | 4.30 GPa | 624 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GS 25 HWCP 25% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |