Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 2.44 GPa @Thickness 6.40 mm |
354 ksi @Thickness 0.252 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL903 PC Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance, excellent impact, flexural strength/rigidity. UV-stabilized. |
|||
Tensile Modulus | 2.44 GPa @Thickness 6.40 mm |
354 ksi @Thickness 0.252 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL900 PC (Asia Pacific) Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance excellent impact, flexural strength/rigidity. UL94 V-1 at .157"" (3.99 mm). |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® OQ1022 PC Standard Flow OQ Resin |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® OQ1022 PC (Asia Pacific) Standard Flow OQ Resin |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® OQ1022 PC (Europe-Africa-Middle East) Standard Flow OQ Resin |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS (Asia Pacific) LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant. |
|||
Tensile Modulus | 2.44 GPa @Thickness 6.40 mm |
354 ksi @Thickness 0.252 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL900 PC Lexan* resin FL900 is a Br- & Cl-free flame retardant grade that can be foamed for weight reductions. UL-94 V1 listed at 3.9mm together with good stiffness, heat, creep and impact performance make i.. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66 Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to h.. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Asia Pacific) Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Europe-Africa-Middle East) Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PVX0901 PPE+PS (Asia Pacific) Multi purpose V1 grade |
|||
Tensile Modulus | 2.44 GPa @Thickness 3.20 mm |
354 ksi @Thickness 0.126 in |
1mm/min; ASTM D638 |
LG Chemical HIPS MI750 PS, Impact Modified Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica.. |
|||
Tensile Modulus | 2.44 GPa | 354 ksi | ASTM D638 |
Amco Amalloy® B9575 Polymer Alloy Amco Amalloy B9575 is a clear performance copolymer with exceptional clarity and toughness.Very clear, high tensile and flexural strength.Information provided by Amco Plastic Materials. |
|||
Tensile Modulus | 2.44 GPa @Thickness 6.40 mm |
354 ksi @Thickness 0.252 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL1000 PC 5% GR. Various weight reductions at .250""(6.35mm) wall. Excellent flex strength/rigidity, high heat/creep resistance. V-0/5VA rated. |