Polymer Property : Tensile Modulus = 289 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	1.99 GPa	289 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Stat-Tech™ PP-16CP/000-2 HI Polypropylene, Unspecified (PP, Unspecified) Stat-Tech™ electrically conductive compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic applications. These compounds combine ..
Tensile Modulus	1.99 GPa	289 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycolac® MG29 ABS Super high impact ABS. Good low temperature toughness. High gloss.
Tensile Modulus	1.99 GPa	289 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycolac® MG29 ABS (Asia Pacific) Super high impact ABS. Good low temperature toughness. High gloss.
Tensile Modulus	1.99 GPa	289 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ HTX Ultra LA425 Polyvinyl Chloride Alloy (PVC Alloy) Optimum for Black and Darker Colors below 50L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Ductile/Brittle transition as measured by Instrumented Impact is 5 de..
Tensile Modulus	1.99 GPa	289 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ HTX Ultra LA426G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss version of Geon HTX Ultra LA426Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426G Black 2880.Information provided by Pol..
Tensile Modulus	1.99 GPa	289 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Tensile Modulus	1.99 GPa	289 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Modulus	1.99 GPa	289 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.