Polymer Property : Tensile Modulus = 1490 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	10.3 GPa	1490 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ NI-30CF/15T-2S Polyamide 610 (Nylon 610) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Modulus	10.3 GPa	1490 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne OnForce™ LFT NN-30 LGF/000 Natural Polyamide 66 (Nylon 66) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Tensile Modulus	10.3 GPa	1490 ksi	ISO 527-1/2
Radici Radilon® CARV300 L (dry) Copolyamide 66/6 Glass-fiber reinforcedInformation provided by Radici group.
Tensile Modulus	10.3 GPa	1490 ksi	ASTM D638
LNP Lubricomp® PDX-O-90351 Polyphenylene Sulfide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Modulus	10.3 GPa	1490 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Stat-Tech™ OC-0307081 Black Acrylonitrile Butadiene Styrene + PC (ABS+PC) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Tensile Modulus	10.3 GPa	1490 ksi	ASTM Data
Dow Questra® EA514 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Modulus	10.3 GPa	1490 ksi	Lengthwise/Crosswise; ASTM D-638
Glastic 1130 Angles, Channels, and Structural Shapes Information provided by Glastic Corporation
Tensile Modulus	10.3 GPa	1490 ksi	ISO 527-1/-2
Lanxess PocanÂ® B 4235 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, flame retardant
Tensile Modulus	10.27 GPa	1490 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OX90351 PPS LNP LUBRICOMP* OX90351 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Tensile Modulus	10.3 GPa	1490 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin.
Tensile Modulus	10.3 GPa	1490 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON SC004 PA 12 (Europe-Africa-Middle East) LNP* Stat-kon* SE004 is a compound based on Nylon 12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Modulus	10.3 GPa	1490 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66 LNP* Thermocomp* RX96592 is a compound based on Nylon 6/6 containing Proprietary Fillers.
Tensile Modulus	10.3 GPa	1490 ksi	ASTM D638
Sumitomo Bakelite DurezÂ® 153 Phenolic, Compression Grade Durez 153 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits good molded appearance and shock resistance for use on a wide variety of electrical a..
Tensile Modulus	10.3 GPa	1490 ksi	ASTM D638
Sumitomo Bakelite DurezÂ® 156 Phenolic, Injection Grade Durez 156 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits excellent dimensional stability, high heat resistance, good molded appearance, and UL..
Tensile Modulus	10.3 GPa	1490 ksi	1 mm/min; ISO 527-1
Sax Polymers SAXAMID 126F7 Nylon 6, 35% Glass Fiber SAXAMID 126F7 is a polyamide 6 injection-molding-grade reinforced with 35% glass fibers. Because of its high strength and stiffness this grade is often used for stressed parts. Additional properties..
Tensile Modulus	10.3 GPa	1490 ksi	ASTM D638
Sumitomo Bakelite DurezÂ® 25378 Phenolic, Compression Grade Durez 25378 Black Phenolic is a two stage heat resistant/electrical grade molding material having an excellent molded finish, low shrinkage and good heat resistance. Durez 25378 has exceptional UL ..
Tensile Modulus	10.3 GPa	1490 ksi	ASTM D638
Plenco 1501 Polyester, Pellet, Injection Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va..
Tensile Modulus	10.3 GPa	1490 ksi	ASTM D638
Plenco 4466 Phenolic, Granular, Injection Molded PLENCO 04466 is a heat resistant, mineral and flock filled phenolic molding compound, offering excellent mechanical strength and cosmetic properties. UL recognized under component file E40654. 04466..
Tensile Modulus	10.3 GPa	1490 ksi	dry; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF10 MX10 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, reinforced with 10% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, good surface quality.T..
Tensile Modulus	10.3 GPa	1490 ksi	1[mm/min]; ISO 527-1/2
Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Tensile Modulus	10.3 GPa	1490 ksi	1[mm/min]; ISO 527-1/2
Akro-Plastic Akromid® B3 GF 50 (2475) PA 6 Conditioned, 50% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Tensile Modulus	10.3 GPa	1490 ksi	same value from ASTM and ISO test.
BASF Capron® 8233G 33% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8233G is a 33% glass fiber reinforced polyamide 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in he..
Tensile Modulus	10.3 GPa	1490 ksi
Radici Radilon® A RV300 990 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Modulus	10.3 GPa	1490 ksi	After Immersion in 50/50 Glycol/Water Mixture for 1,000 hours at 275°F (135°C); ASTM D638
Solvay Specialty Polymers Amodel® AS-1945 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-1945 HS is a 45% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material excee..
Tensile Modulus	10.3 GPa	1490 ksi	Lengthwise/Crosswise; ASTM D-638
Glastic GLASGUARD 1130 Corrosion-Resistant Panels GlasGuard Grade 1130 is a fiberglass-reinforced thermoset polymer composite system which is available as sheet stock or in a variety of pultruded shapes. Grade 1130 possesses flame resistance, corr..