Polymer Property : Tensile Modulus = 9.20 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	9.20 GPa	1330 ksi
Plastcom SLOVAMID 6 GF 30 FRA 3 PA6, 30% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with halogen flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 850°C,..
Tensile Modulus	9.20 GPa	1330 ksi	ISO 527-1/-2
Quadrant EPP Ketron® CA30 PEEK + carbon fibres, extruded (ISO Data) This 30 % carbon fibre reinforced grade combines even higher stiffness, mechanical strength and creep resistance than Ketron PEEK-GF30 with an optimum wear resistance. Moreover, compared with unrein..
Tensile Modulus	9.20 GPa	1330 ksi	ISO 527
Nilit FRIANYL A63 HS-GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced Nylon 6.6 for injection molding, high impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Modulus	9.20 GPa	1330 ksi	ISO 527-1/-2
DSM Akulon® S224-KMV7 Nylon 66-35% Mineral Reinforced (European and Asian Grade) (Dry) (discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Modulus	9.20 GPa	1330 ksi	ISO 527-1/-2
Lanxess DurethanÂ® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, improved notched impact strength and energy absorption under biaxial impact load, good heat-ageing resistance
Tensile Modulus	9.20 GPa	1330 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® R AR 130/GF Nylon 66, 30% glass fiber, DRY Description: TECHNYLÂ® AR 130/GF is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. It contains recycled raw materials. This product is available in bla..
Tensile Modulus	9.20 GPa @Temperature 100 Â°C	1330 ksi @Temperature 212 Â°F	4; ISO 527-2
Solvay Specialty Polymers AmodelÂ® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) AmodelÂ® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in..
Tensile Modulus	9.20 GPa	1330 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66 LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive.
Tensile Modulus	9.20 GPa	1330 ksi	1 mm/min; ISO 527-1
Sax Polymers SAXAMID 126F6 Nylon 6, 30% Glass Fiber SAXAMID 126F6 is a polyamide 6 injection-molding-grade reinforced with 30% glass fibers. Because of its high strength and stiffness this grade is often used for stressed parts. Other properties are ..
Tensile Modulus	9.20 GPa	1330 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East) Post-industrial recycle based, 30% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Modulus	9.20 GPa	1330 ksi	ASTM D638
Plenco 6582 Phenolic, Briquette, Transfer Molded PLENCO 06582 is a rubber modified phenolic molding compound, offering excellent heat resistant properties, along with improved mechanical strength at elevated temperatures. UL recognized under compo..
Tensile Modulus	9.20 GPa	1330 ksi	dry; ISO 527-1/-2
DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17) 20% Glass Reinforced, Flame Retardant
Tensile Modulus	9.20 GPa	1330 ksi	ISO 527-1/-2
DuPont Performance Polymers Crastin® LW9030 BK851 PBT+ASA (Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030 BK851 is a 30% glass fiber reinforced black polybutylene terephthalate blend for injection mol..
Tensile Modulus	9.20 GPa	1330 ksi	1 mm/min; ISO 527
Eurostar Starflam AFR450B PA66, 25% Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR450B is a Flame Retardant, 25% Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Tensile Modulus	9.20 GPa	1330 ksi	1mm/min; ISO 527
BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Dry) Ultramid 7523-2AM BK ND3007 is an impact modified, 33% glass reinforced, heat stabilized injection molding PA6/6.