Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 8.76 GPa | 1270 ksi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ NN-30GF/13T-2S Black Polyamide 66 (Nylon 66) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Tensile Modulus | 8.76 GPa | 1270 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 LNP LUBRILOY* RF206 is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material includes: Wear Resistant. |
|||
Tensile Modulus | 8.76 GPa | 1270 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY RF206AXH PA 66 LNP LUBRILOY* RF206AXH is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material include: Wear Resistant, Healthcare. |
|||
Tensile Modulus | 8.76 GPa | 1270 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DX13354 PC COPOLYMER (Asia Pacific) DX13354 is 30% glass fiber reinforced, impact modified and LDS functionalized polycarbonate resin. The features include LDS function, high flow, and good ductility. |
|||
Tensile Modulus | 8.76 GPa | 1270 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS resin containing 30% Glass Fiber. |
|||
Tensile Modulus | 8.76 GPa | 1270 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 LNP* THERMOCOMP* SF008 is a compound based on Nylon 12 resin containing 40% Glass Fiber. |
|||
Tensile Modulus | 8.76 GPa | 1270 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific) LNP* Thermocomp* SF008 is a compound based on Nylon 12 resin containing Glass Fiber. |