Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 6.37 GPa | 925 ksi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact PC/GF material that is used for electric and electronic partsInformation provided by Samsung Cheil Industries. |
|||
Tensile Modulus | 6.37 GPa | 924 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10 LNP* THERMOCOMP* QF004 is a compound based on Nylon 6/10 resin containing 20% Glass Fiber. |
|||
Tensile Modulus | 6.37 GPa | 924 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF004 is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Tensile Modulus | 6.37 GPa | 924 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
Tensile Modulus | 6.37 GPa | 924 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific) LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
Tensile Modulus | 6.37 GPa @Temperature -40.0 °C |
924 ksi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry) Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the.. |
|||
Tensile Modulus | 6.37 GPa | 925 ksi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact PC/GF material that is used for electric and electronic partsInformation provided by Samsung Cheil Industries. |