Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 5.79 GPa | 840 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2212EPR PEI 20% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA lising. |
|||
Tensile Modulus | 5.79 GPa | 840 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2212EPR PEI (Asia Pacific) 20% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA lising. |
|||
Tensile Modulus | 5.79 GPa | 840 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6 LNP THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Modulus | 5.79 GPa | 840 ksi | 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp TX88477 PU LNP* Thermocomp* TX88447 is a compound based on Polyurethane resin containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 5.79 GPa @Temperature 175 °C |
840 ksi @Temperature 347 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry
(discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg.. |