Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.85 GPa | 268 ksi | |
Plastcom SLOVALEN PQ 81 T 30 PP, 30% mineral filling FeaturesModified PP for injection moulding with the content of 30% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1 mm/min; ISO 527 |
Polimeri Europa Edistir R 850E Polystyrene Super high impact polystyrene with good heat resistance. Designed for sheet extrusion and thermoforming of deep drawn containers even
diluted with high percentage of GP. Suitable for general injecti.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers RIGITRON 10001 Polycarbonate PC – Impact Modified, high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-1/2 |
Radici Radilon® AUSX200 (dry) Nylon 66 Very high impact strengthInformation provided by Radici group. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS (Asia Pacific) LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing PTFE. Added features of this material include: Internally Lubricated, High Impact. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1 mm/min |
Polimeri Europa KOBLEND HI 20 PBT+PC, Impact Grade
(discontinued **) PBT elastomer modified with good impact behaviour, good stiffness, resistant to solvents. Main application fields: automotive industryUnfilled. Suitable for Injection Molding. Supplied as pellets.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min |
Eastman Eastalloy DA105 PC+PET Copolyester/Polycarbonate
(discontinued **) ISO data as provided by the manufacturer, Eastman Chemical |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min |
Eastman Tenite 371A-08 Cellulose Acetate Propionate
(discontinued **) 8% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | |
Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping be.. |
|||
Tensile Modulus | 1.85 GPa @Temperature 23.0 °C |
268 ksi @Temperature 73.4 °F |
|
LATI Lastilac MR MDT05-01 ABS Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Magnetic detectable filler. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North .. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527 |
Styrolution PS 476L HIPS Styrolution PS 476L is a normal flow and very high impact Polystyrene. It gives good mechanical and heat resistance properties while providing with easy processability and short cycle time.Normal fl.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP M7002XXH PP LNP* THERMOCOMP* M7002XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additives. Designed for touch surfaces in healthcare applications. Added features include:.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | At 1 mm/min; ISO 527-2 |
Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled Daplen EE137AI is a 10% mineral filled grade intended for injection molding. EE137AI has been developed especially for the car industry, to be used in interior parts where high scratch resistance i.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min; ISO 527-2 |
Borealis Daplen™ EE188HP Polypropylene TPO Compound Daplen™ EE188HP is a 15% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and g.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-2 |
Total PPH 12020 Polypropylene Homopolymer, Injection Molding Polypropylene PPH 12020 is a clarified high fluidity homopolymer with a melt flow index of 60 g/10 min.Polypropylene PPH 12020 has been designed with a very high stiffness and an outstanding transpa.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min; ISO 527-2 |
Borealis Daplen™ EE188AI Polypropylene TPO Compound Daplen™ EE188AI is a 15% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. .. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min; ISO 527-2 |
Borealis Daplen™ EE189AI Polypropylene TPO Compound Daplen™ EE189AI is a 15% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. .. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-1/-2 |
DSM Stanyl® TW363 (DAM) Nylon 46 Heat Stabilized, Impact Modified (North America) Information provided by DSM Engineering Plastics. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-1/-2 |
DSM Stanyl® TW363 Nylon 46 (European Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 100TE NC010 Acetal (POM)
(Unverified Data**) Toughened High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 100TE NC010 (formerly DE20580) is a high viscosity toughened acetal homopolymer with very low VOC emissions. Processing met.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | Storage |
Epoxy Technology EPO-TEK® U300-2 Two Component Epoxy Material Description: A two component epoxy designed for capillary underfill of semiconductor chips and SMDs. Long potlife, high Tg, and optical clarity are a few of its traits. NASA approved lo.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TR 90 TL PAMACM12 Product description: Grilamid TR 90 TL is a transparent thermoplastic polyamide based on aliphatic, cycloaliphatic and aromatic blocks. The special characteristic of Grilamid TR 90 TL is the high st.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | ASTM D638 |
Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness) AZDEL SuperLite® SL550800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | |
BASF Polystyrol® 475 K Impact Grade Polystyrene (Europe) Normal flowing, high-impact grade with particularly good creep strength.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | |
BASF Polystyrol® 476 L Impact Grade Polystyrene (Europe) Normal flowing, high-impact grade. When extruded it is often mixed with PS 165 H.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP CL001I PS LNP* Lubricomp* CL001I is a compound based on Polystyrene resin containing 5% PTFE. Added features of this material include: Internally Lubricated, High Impact. |
|||
Tensile Modulus | 1.85 GPa | 268 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® VX3608C PBT (Europe-Africa-Middle East) VALOX VX3608C is an impact modified, flame retardant PBT+PC injection moulding resin. Application: electrical enclosures. This grade is 3607U with reduced oxygen index.This data was supplied by SABI.. |