- Polymer Property : Tensile Strength, Yield = 5.00 MPa
Polymer Property : Tensile Strength, Yield = 5.00 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ISO 527 |
| Polimeri Europa Clearflex® MP D0 Very Low Density Polyethylene Clearflex MP D0 is a linear polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin shows an excellent balance between flexibility and impact resistance.Main Applicati.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ISO 527 |
| Polimeri Europa Greenflex® MP 35 Ethylene Vinyl Acetate Copolymer - Injection Molding & Extrusion Greenflex MP 35 is an ethylene vinyl acetate copolymer (EVA) for injection molding and extrusion. Greenflex MP 35 is an easy flowing material and provides a very high elasticity.Main Applications: .. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D412 |
| Precision Polymer Engineering E70H Ethylene Propylene Rubber Peroxide cured, white Ethylene Propylene Terpolymer, 66-75 °IRHD. Terpolymer of ethylene, propylene and diene monomers. Formulated using only those ingredients determined by the United States Fede.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D412 |
| Precision Polymer Engineering E70Z Ethylene Propylene Rubber Peroxide cured, grey Ethylene Propylene Terpolymer, 65-75 °IRHD. Terpolymer of ethylene, propylene and diene monomers. Specially formulated for sealing applications involving high voltage electri.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | 50% Elongation; ASTM D412 |
| Covestro Texin® DP7-3008 Thermoplastic Polyurethane, Polyester-based, Aliphatic
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D638 |
| Petroquimica Triunfo Tritheva® TN 8093 EVA Copolymer The Tritheva TN 8093 resin is a fractional MI copolymer of Ethylene-Vinyl Acetate (EVA), developed to meet the multi-layer and blending film applications where are required high strength, with high .. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | 150°C for 1,000 hrs; JIS-K-6251 |
| Fujipoly Industries Sarcon® 25G-Td Thin-Film GR-TD Sarcon 25G-Td is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary.Information provided by Fujipoly Industries |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ISO 527-1, -2 |
| LyondellBasell Adflexâ„¢ Q 100 F Polyolefin Description: Adflexâ„¢ Q 100 F is a thermoplastic polyolefin which has been developed for the extrusion of blown film, it is also suitable for sheet extrusion. Adflexâ„¢ Q 100 F features a ver.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp XL004 Amorphous Polyamide LNP* Lubricomp* XL-4040 is a compound based on Amorphous Nylon, containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | Elastic Limit |
| Wolf Kunststoff ZEDEX® ZX-100EL63 A1G Polymer Alloy, Elastomer Modified Main Characteristics: Rubbery; Soft; High shock absorption; High impact resistance; Elongation > 300%Applications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technol.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | |
| Trelleborg Commercial Neoprene® C722 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | |
| Trelleborg E849 EPDM Rubber EPM -- EPDM or Ethylene -- Propylene Rubber. EPM can only be vulcanized by peroxides or radiation; whereas EPDM can be vulcanized conventionally using sulphur.Properties:Excellent inherent high and .. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | |
| Trelleborg R661 Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
| Tensile Strength, Yield | 5.00 MPa @Temperature 21.1 °C |
725 psi @Temperature 70.0 °F |
Flatwise Tensile; After 500 hrs at 400°F (Weight loss = 0.75%); Composite Honeycomb Sandwich Performance; ASTM C 297 |
| Hexcel® Redux® HP655 Toughened BMI film Adhesive Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655.. |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 100 % |
725 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® 3485A Polyurethane Extrusion- and injection molding gradesuitable for extrusion blow moldingwith release agenthigh melt stabilityApplicationBellowsInjection molded engineering partsPreprocessingMax. Water content |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 100 % |
725 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® 481 Polyurethane injection molding gradefree from plasticizersgrease and oil-resistantlow compression sethigh elasticitygood heat resistanceEasy releaseApplicationRoller coatingSealsmembranesAutomotive engineeringPr.. |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 100 % |
725 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® DP 1485A Polyurethane Extrusion- and injection molding gradesuitable for extrusion blow moldingvery large processing windowhigh melt stabilityBeadsApplicationBellowsHosesnon-reinforcedProfilesInjection molded engineering.. |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 300 % |
725 psi @Strain 300 % |
ISO 527-1/-2 |
| Covestro Desmopan® DP 1966AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 100 % |
725 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® DP 8785 A Polyurethane injection molding gradewith special UV stabilizersEasy releaseshort cycle timesApplicationSports shoe solesPreprocessingMax. Water content |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 100 % |
725 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® DP 8785A S043 Polyurethane injection molding gradewith special UV stabilizersexcellent abrasion resistanceEasy releaseshort cycle timesApplicationSports shoe solesPreprocessingMax. Water content |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 50.0 % |
725 psi @Strain 50.0 % |
|
| Covestro Texin® 285 Urethane Thermoplastic Elastomer Key Features:UnfilledSuitable processing methods:Injection moldingFilm extrusionProfile extrusionSheet extrusionCoatingBlow moldingInformation provided by Bayer Polymers.As of 1 September 2015, Baye.. |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 50.0 % |
725 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKS 918 R PVC, Soft Extrusion Grade NAKAN FKS 918 R is a soft polyvinyl chloride compound developed for general insulation and sheathing.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 5.00 MPa @Strain 50.0 % |
725 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FSS 601 R PVC, Soft Injection Molding Grade NAKAN FSS 601 R is a soft polyvinyl chloride compound developed for injection molding of transparent soling ( very clear ).ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | |
| BASF Lucalen® A 3110 M Q 244 Ethylene/Acrylate Copolymer Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | |
| ACC MM240T Addition Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: cures at room temperature, low shrinkage, high tear and tensile strengths. Applications: rapid prototyping. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | 50 mm/min |
| Arkema Group Evatane® 1090 VN 3 Ethylene Vinyl Acetate Description: EVA copolymer made by high pressure tubular process.Applications:Grade for molding flexible articles.Examples: Closures, plugs, swimming flippers, toys.ISO data provided by the manufact.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D638 |
| ExxonMobil Escorene® LD-728 High EVA Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.Applications: Injection molding; Foams.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D638 |
| ExxonMobil Escorene® LD-730 High EVA Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.Applications: Injection molding; Foams.. |
|||
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ISO 527 |
| Breplast Bretene SPF Thermoplastic Composite, 40% PP + 60% PE Recovered polypropylene and polyethylene compositeInformation provided by Breplast S.p.A. |
|||