Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	1060 - 1170 MPa	154000 - 170000 psi	Solution Annealed & Aged
Materion Beryllium Copper Alloy 245C Castings (UNS C82600) Pouring Temperature: 970-1065Â°CHeat treatment required for max strength (Annealing): 760-790Â°C/water quenchHeat treatment required for max strength (Hardening): 760-790Â°C/water quenchTabula..
Tensile Strength, Yield	1165 - 1172 MPa @Strain 0.200 %	169000 - 170000 psi @Strain 0.200 %
Latrobe LescalloyÂ® UT-18 VAC-ARC ; 3.75 in. round High Strength Alloy Steel UT-18 VAC-ARC is a medium-carbon, low-alloy heat resistant steel having high strength to 1000Â°F. It is used primarily for turbine and compressor rotor shafts. Vacuum consumable electrode melting..
Tensile Strength, Yield	1145 - 1172 MPa @Strain 0.200 %	166100 - 170000 psi @Strain 0.200 %
Latrobe LescalloyÂ® UT-18 VAC-ARC ; 4 in. round High Strength Alloy Steel UT-18 VAC-ARC is a medium-carbon, low-alloy heat resistant steel having high strength to 1000Â°F. It is used primarily for turbine and compressor rotor shafts. Vacuum consumable electrode melting..
Tensile Strength, Yield	1060 - 1170 MPa	154000 - 170000 psi	Solution Annealed & Aged
Materion Beryllium Copper Alloy 245CT Castings (UNS C82600) Pouring Temperature: 970-1065Â°CHeat treatment required for max strength (Annealing): 760-790Â°C/water quenchHeat treatment required for max strength (Hardening): 760-790Â°C/water quenchTabula..
Tensile Strength, Yield	793 - 1172 MPa	115000 - 170000 psi
Materion Beryllium Nickel Strip - Alloy 360 1/2 Hard Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedFormability Ratio, 90Â° Bend, Radius/Thickness (Good Way): 0.7Formability Ratio (bad Way)..
Tensile Strength, Yield	1138 - 1172 MPa @Strain 0.200 %	165100 - 170000 psi @Strain 0.200 %	Core heat treated from 1850Â°F
Latrobe CBS-223â„¢ VIM-VAR Carburizing Bearing and Gear Steel CBS-223 VIM-VAR steel is a double vacuum melted carburizing steel with high hot hardness characteristics. Double vacuum melting sequentially combines vacuum induction melting with VACARCâ„¢ remel..