- Polymer Property : Tensile Strength, Yield = 9250 psi
Polymer Property : Tensile Strength, Yield = 9250 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.8 MPa | 9250 psi | ASTM D638 |
| Polymer Resources PPX-G5 Modified-PPO, 5% Glass Reinforced Modified-Polyphenylene Oxide, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro.. |
|||
| Tensile Strength, Yield | 63.8 - 167 MPa | 9250 - 24200 psi | Average value: 89.5 MPa Grade Count:7 |
| Overview of materials for Polyphenylene Ether, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 10% Glass Filled". Specific grades with glass content between 5% and 14% are includ.. |
|||
| Tensile Strength, Yield | 63.8 MPa | 9250 psi | ISO 527-2 |
| Solvay Specialty Polymers Ixef® BXT-2000/0203 Polyarylamide (PARA)
(Unverified Data**) Ixef BXT-2000/0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef BXT-2000/0203 resin can be successfully extruded into.. |
|||
| Tensile Strength, Yield | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| LG Chemical LUCON CP6052 PC/ABS+CNT Description Injection Molding Grade, PC/ABS+CNT, Electrostatic Dissipation, Low Surface Resistivity, Improved Impact StrengthApplication: Laser diode Tray, ATM parts, Telecommunication Station Housi.. |
|||
| Tensile Strength, Yield | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUMID HI1102B(W) PA66, High Impact Feature: Injection Molding,PA66, High ImpactApplication: Automotive (Covers)CAS No. 32131-17-2 and 9010-79-1Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 63.8 MPa | 9250 psi | ISO 527-2 |
| Solvay Specialty Polymers Ixef® BXT 2000-0203 Polyarylamide (PARA) Ixef® BXT 2000-0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef® BXT 2000-0203 resin can be successfully extru.. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® FD-1122 PC, FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® HR-8070 MPPE, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NE-1010 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NF-3017 PC/ABS, Unreinforced FR Flame-retardant scratch resistant material that can be used in notebook B partInformation provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NH-1014S PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® SC-1100R PC, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Starex® TH-1100 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® FD-1122 PC, FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® GC-1150 PC/ABS, FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® HR-8070 MPPE, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NE-1010 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NF-3017 PC/ABS, Unreinforced FR Flame-retardant scratch resistant material that can be used in notebook B partInformation provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NH-1014S PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® SC-1100R PC, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Starex® TH-1100 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® GC-1150 PC/ABS, FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | ASTM D638 |
| Cheng Yu Plastic PP238G3 Polypropylene, 30% Glass Fiber |
|||