- Polymer Property : Tensile Strength, Yield = 9000 psi
Polymer Property : Tensile Strength, Yield = 9000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP3-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold Release Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samp.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP4-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Easy Flow Polycarbonate, FDA-compliant Feedstocks, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-FR7 Modified-PPO, V-0 Flame Retardant Modified-Polyphenylene Oxide, V-0 Flame Retardant, 260F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-GP5 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 270F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources NY6-IM1-[color]H Nylon, Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| PolyOne Therma-Tech™ SFC-5000 TC Polyphenylene Sulfide (PPS)
(discontinued **) Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Global PC-1410 General Purpose Polycarbonate Information provided by Global Polymers Corporation. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Global PC-FR0 UL Recognized 94V-0 Polycarbonate Information provided by Global Polymers Corporation. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | 2.0 in/min; ASTM D638 |
| LTL Color Compounds ColorFast® PC150 Polycarbonate 15 melt high flow polycarbonateAll information provided by LTL Color Compounders, Inc. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Fiberfil® J-60/15/UV/HS Polypropylene Homopolymer, 15% Glass Reinforced, Heat Stabilized, UV Stabilized Information provided by FIBERFIL Engineered Plastics |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES Electrablend® ABS CF5 5% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 5% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES HiFill FR® PA6/6 FR 144 Availability: North AmericaForms: PelletsAdditive: Lubricant and Heat StabilizerFeatures: Flame Retardant, Halogen Free, Heat Stabilized and LubricatedInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES HiFill FR® PA6/6 FR 346 RD Availability: North AmericaForms: PelletsAdditive: Lubricant and Heat StabilizerFeatures: Flame Retardant, Heat Stabilized and LubricatedAppearance: RedInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES HiFill® HIPS GF15 15% Glass Filled Availability: North AmericaForms: PelletsGlass Fiber Reinforcement, 15% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES HiFill® PA11 GL8 HS UV Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Graphite Powder Lubricant and UV StabilizerFeatures: Heat Stabilized. Good UV Resistance and LubricatedAppearance: Natural ColorIn.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Spartech Noryl® GTX SP-52Z1 Structural Sheet Description: Structural SheetNoryl is a registered trademark of General Electric Company.Information provided by Spartech. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES HiFill® PA6/6 GF8 IM4 HS L 8% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 8% Filler by WeightAdditive: LubricantFeatures: Lubricated Appearance: BlackInformation provided by TP Compo.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Star Plastics PC743 Molding Grade PC Information provided by Star Plastics, Inc. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES Luriblend® PA6 TS15 BK Nylon 6 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Silicone Lubricant and PTFE LubricantFeatures: Heat Stabilized and LubricatedAppearance: BlackInformation provided by TP Composite.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ISO 527 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Chase Plastics CP Pryme® PC300RHF Polycarbonate, Recycled Content Features: Good flowHigh rigidityGood toughnessHigh strengthLow viscosityGood mold releaseRecycled contentForm: PelletsInformation provided by Chase Plastics. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ISO 527 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D 638 |
| A. Schulman COMTUF® 506 Polycarbonate Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ISO 527 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ISO 527 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Clariant Renol 6253 Nylon 6, High Impact Data provided by Clariant Masterbatches |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Clariant Renol PA2SP0017 Nylon 6, Impact Modified Data provided by Clariant Masterbatches |
|||
| Tensile Strength, Yield | 62.1 MPa @Strain <=1.00 % |
9000 psi @Strain <=1.00 % |
Silicone Property; Arlon SQA-TMS-008 |
| Arlon Thermabond® 99A90X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Description: Primerless Thermabond®: Electrically insulating, thermally conductive, electronic adhesive. Bonds without primer.Design/Construction: Liner: FEPProduct: Uncured Silicone Rubber Carrier.. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-FR7 Modified PPO, V-0 Flame Retardant, Medium Heat, 250 HDT
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | 2.0 in/min; ASTM D638 |
| LTL Color Compounds ColorFast® FRPC100 Polycarbonate, Flame-Retarded Flame-retarded V0, high impact injection molding polycarbonateAll information provided by LTL Color Compounders, Inc. |
|||