Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 595 MPa @Strain 0.200 % |
86300 psi @Strain 0.200 % |
|
Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 595 MPa @Strain 0.200 % |
86300 psi @Strain 0.200 % |
|
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 595 MPa @Strain 0.200 %, Temperature 425 °C |
86300 psi @Strain 0.200 %, Temperature 797 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Yield | 595 MPa @Strain 0.200 %, Temperature 760 °C |
86300 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 595 MPa @Strain 0.200 % |
86300 psi @Strain 0.200 % |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |