Polymer Property : Tensile Strength, Yield = 812 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	5.60 MPa	812 psi	ISO 527
Polimeri Europa Greenflex® MH 40 Ethylene Vinyl Acetate Copolymer - Injection Molding & Extrusion Greenflex MH 40 is an ethylene vinyl acetate copolymer (EVA) for injection molding and extrusion. Items produced with Greenflex MH 40 show high elasticity and good mechanical properties.Main Applic..
Tensile Strength, Yield	5.60 MPa	812 psi	-20% change after 70 hours @ 70°C; ASTM D412
Precision Polymer Engineering N40M Nitrile Rubber Nitrile Butadiene Rubber, 35-45 °IRHD. Medium acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet British Standard BS2751 BA40.Applications: Excellent resistance to petro..
Tensile Strength, Yield	5.60 MPa	812 psi	-20% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N90L Nitrile Rubber Low Nitrile Rubber, 85-95 °IRHD. Low acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. ASTM designation = NBR. ISO designation = NBR. ASTM D2000 line call-out M6BG907, A14, B..
Tensile Strength, Yield	5.60 - 10.4 MPa	812 - 1510 psi	±30% change after 168 hours @ 70°C; ASTM D412
Precision Polymer Engineering R90B Natural Rubber Natural Rubber, 85-95 °IRHD. This material is based on high-quality plantation (Hevea) rubber, reinforced with carbon black.Applications: Natural rubber offers low compression set, high tensile st..
Tensile Strength, Yield	5.60 MPa	812 psi	ASTM D412
Precision Polymer Engineering S50A Silicone Rubber Blue Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent heat resistance and low temperature flexibility. Use..
Tensile Strength, Yield	5.60 MPa	812 psi	-20% change after 336 hours @ 200°C; ASTM D412
Precision Polymer Engineering S50D Silicone Rubber Black Silicone Rubber, 46-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated to meet UK Ministry of Defence Aircraft Materials Specificatio..
Tensile Strength, Yield	5.60 MPa	812 psi	ASTM D412
Precision Polymer Engineering S50G Silicone Rubber Green Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent heat resistance and low temperature flexibility. Us..
Tensile Strength, Yield	5.60 MPa	812 psi	ASTM D412
Precision Polymer Engineering S50Y Silicone Rubber Yellow Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent heat resistance and low temperature flexibility. U..
Tensile Strength, Yield	5.60 MPa	812 psi	M100
3M Dyneon™ Fluorel™ FG-5630Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. When compared to other food grade Dia..
Tensile Strength, Yield	5.60 MPa	812 psi	M100
3M Dyneon™ Fluorel™ FC-2145 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp..
Tensile Strength, Yield	5.60 MPa	812 psi	Film Property, 50 µm thickness; ASTM D882
Arkema Group OREVAC® 9307 Y EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..