Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 455 MPa | 66000 psi | |
Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Yield | 455 MPa | 66000 psi | |
Mueller Dynalloy Alloy 6730 Free cutting bearing bronze (UNS C67300) Free cutting bearing bronzeApplications: Dynalloy is widely used for bearing applications, bushings, gears, valve guides, shaft and cylinder guides. The alloy has found wide acceptance in speed red.. |
|||
Tensile Strength, Yield | 455 MPa @Strain 0.200 % |
66000 psi @Strain 0.200 % |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 455 MPa @Strain 0.200 % |
66000 psi @Strain 0.200 % |
|
Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 455 MPa @Strain 0.200 % |
66000 psi @Strain 0.200 % |
As-Consolidated; At Room Temperature |
Crucible Compaction Metals P/M N625 Corrosion Resistant Alloy P/M N625 (chemically, UNS N06625) is produced by the state-of-the-art Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The a.. |
|||
Tensile Strength, Yield | 455 MPa @Temperature 93.0 °C |
66000 psi @Temperature 199 °F |
|
ATI Allegheny Ludlum AL 2003™ Duplex Stainless Steel Characteristics: superior stress corrosion cracking resistance to Types 316 and 317, yield strength double that of conventional austenitic stainless steel, good corrosion resistance, good chloride s.. |