Polymer Property : Tensile Strength, Yield = 60900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	420 MPa @Strain 0.200 %	60900 psi @Strain 0.200 %
Haynes 556Â® alloy, bar, after 1000 hours at 760Â°C (1400Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	420 MPa @Strain 0.200 %	60900 psi @Strain 0.200 %
Haynes HastelloyÂ® B-3Â® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Yield	420 - 490 MPa @Strain 0.200 %	60900 - 71100 psi @Strain 0.200 %
SSAB Tunnplat Aluzink 420A YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Aluzink YP - HSLA steel (aluminum-zinc coated sheet). Property values are for thicknesses 0.4 - 2.0 mm. Iron content is approximate - exact composition is ..
Tensile Strength, Yield	420 - 540 MPa @Strain 0.200 %	60900 - 78300 psi @Strain 0.200 %
SSAB Tunnplat DocolÂ® 420YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report..
Tensile Strength, Yield	420 - 490 MPa @Strain 0.200 %	60900 - 71100 psi @Strain 0.200 %
SSAB Tunnplat Dogal 420YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Dogal YP - HSLA steel. Property values are for thicknesses 0.4 to 2.5 mm. Iron content is approximate - exact composition is not reported by the manufactur..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi
SSAB Tunnplat DomexÂ® 420MC HSLA Steel HSLA SteelCharacteristics: Some thicknesses of these steel grades are available with a maximum of 0.03% Si for thin Zn coating. If the material is to be hot-dip galvanized and steel with a maximum ..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi
SSAB Tunnplat DomexÂ® 420XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: DomexÂ® is the brand name of hot rolled products from SSAB Tunnplat. DomexÂ® cold-forming steels are modern structural steels. Gene..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi
SSAB Tunnplat DomexÂ® 420YP Cold-forming Steel, HSLA Cold-forming Steel, HSLACharacteristics: DomexÂ® is the brand name of hot rolled products from SSAB Tunnplat. DomexÂ® cold-forming steels are modern structural steels. General use of DomexÂ®..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi
ThyssenKrupp PAS 420 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio..
Tensile Strength, Yield	420 - 520 MPa	60900 - 75400 psi
ArcelorMittal HSLA 420 High strength low alloy steel for cold forming, Cold Rolled Available in the following: uncoated (HC420LA), electroglavanized (HC420LA +ZE) and Extragal®/galfan/Galvannealed (HC420LA+Z/+ZA/+ZF)Description: Steels in the HSLA (High Strength Low Alloy) range ..
Tensile Strength, Yield	420 - 500 MPa	60900 - 72500 psi
ArcelorMittal HSLA 420 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S420MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi
AK Steel ASTM A 1011, Class 1 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA) Information provided by AK Steel
Tensile Strength, Yield	420 MPa	60900 psi
ThyssenKrupp TBL PLUS Structural Steel This Material Specification applies to heavy plate with thicknesses up to 12 mm, made of the fine-grain structural steel TBL PLUS.Application: The steel may be used for welded constructions of diffe..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi	50<x=60mm
ThyssenKrupp XABO® 460 Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..
Tensile Strength, Yield	420 MPa @Strain 0.200 %	60900 psi @Strain 0.200 %
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Tensile Strength, Yield	420 MPa @Strain 0.200 %	60900 psi @Strain 0.200 %
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Tensile Strength, Yield	>= 420 MPa	>= 60900 psi	50<x=60mm
ThyssenKrupp XABO® 460 T Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..
Tensile Strength, Yield	420 MPa @Strain 0.200 %	60900 psi @Strain 0.200 %
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..