Polymer Property : Tensile Strength, Yield = 54000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	372 MPa	54000 psi
Niagara LaSalle 1018 Cold Finished Steel Bar This low carbon steel has good case hardening properties. Although not classed as a screw machine steel, at times it may be specified. This is an excellent steel for bending and cold forming, with g..
Tensile Strength, Yield	372 MPa @Temperature 23.9 °C	54000 psi @Temperature 75.0 °F	0° Direction, Dry; ASTM D638 Type 1
Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-722 is a modified 350°F cure epoxy system with excellent processing characteristics for vacuum bag, press, and autoclave molding.Key Features and Benefits:Epoxy resin system optimized f..
Tensile Strength, Yield	372 MPa @Strain 0.200 %	54000 psi @Strain 0.200 %
Haynes MultimetÂ® alloy, sand cast, 1171Â°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Yield	372 MPa @Strain 0.200 %, Temperature 93.0 Â°C	54000 psi @Strain 0.200 %, Temperature 199 Â°F
Haynes HastelloyÂ® C-22Â® alloy, 0.71-3.2 mm thick sheet, solution heat treated HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Yield	372 MPa @Strain 0.200 %, Temperature 538 Â°C	54000 psi @Strain 0.200 %, Temperature 1000 Â°F
Haynes HastelloyÂ® C-22Â® alloy, all-weld metal, GMAW short arc HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Yield	372 MPa @Strain 0.200 %	54000 psi @Strain 0.200 %
Special Metals INCONELÂ® 690 Nickel Superalloy, Hot Rolled Flat, 0.62 inch (16 mm) Diameter Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Hot Rolled Flat, 0.62 in..
Tensile Strength, Yield	372 - 483 MPa	54000 - 70000 psi	0.2% offset
Eagle Brass 18665 MSP1, 1/2 Hard MSP-1 high performance copper alloy with magnesium has high conductivity (63% IACS), high strength and excellent thermal creep properties. Typical uses include terminals, connectors, relays, springs..
Tensile Strength, Yield	372 - 455 MPa	54000 - 66000 psi	0.2% offset
Eagle Brass 19210 XP-10 Copper Iron, Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f..
Tensile Strength, Yield	372 MPa	54000 psi	Proportional Limit
ECOMold 135 Copper Mold Material ECOMold® copper alloys (beryllium-free) are engineered specifically for plastics industry applications. ECOMold® 135 has superior thermal conductivity compared to other common mold materials. T..
Tensile Strength, Yield	372 MPa @Strain 0.200 %	54000 psi @Strain 0.200 %
AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala..
Tensile Strength, Yield	372 MPa @Strain 0.200 %	54000 psi @Strain 0.200 %
Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Yield	372 MPa @Strain 0.200 %	54000 psi @Strain 0.200 %
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Tensile Strength, Yield	372 MPa @Strain 0.200 %	54000 psi @Strain 0.200 %
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..