Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 350 - 460 MPa @Strain 0.200 % |
50800 - 66700 psi @Strain 0.200 % |
after heat treatment |
PEAK Werkstoff DISPAL S691 Aluminum Alloy, AlCu5Ti High stiffness and elongation at ruptureInformation provided by PEAK Werkstoff GmbH |
|||
Tensile Strength, Yield | 350 MPa | 50800 psi | |
Kennametal Stellite Deloro® 40G Nickel base. Good combination of wear resistance, corrosion resistance, machinability, and repairability. Machined with tungsten carbide tools, using slow speeds and light feeds. Finish grinding ach.. |
|||
Tensile Strength, Yield | 350 MPa | 50800 psi | Proof Stress |
Kennametal Stellite Denertiaâ„¢ N8 Nickel Dental Alloy Denertiaâ„¢ N8 is a low-carbon nickel based porcelain-bonding alloy for the manufacture of dental crowns and bridges.This alloy is Beryllium and Cadmium free as defined by ISO 22674Information pr.. |
|||
Tensile Strength, Yield | 350 MPa | 50800 psi | |
MMCC Aluminum/SiC 55p Aluminum Matrix Composite Cast, discontinuously reinforced aluminum matrix composite. May be fabricated by vacuum infiltration of the ceramic preform.Data provided by the manufacturer, Metal Matrix Cast Composites (MMCC). |
|||
Tensile Strength, Yield | >= 350 MPa | >= 50800 psi | |
MetalTek MTEK 50-50Nb Cast UNS R20501 Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 % |
50800 psi @Strain 0.200 % |
|
Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 % |
50800 psi @Strain 0.200 % |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 % |
50800 psi @Strain 0.200 % |
|
Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 350 MPa @Temperature 870 °C |
50800 psi @Temperature 1600 °F |
|
Haynes Hastelloy® alloy 188 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 %, Temperature 650 °C |
50800 psi @Strain 0.200 %, Temperature 1200 °F |
|
Special Metals UDIMET® alloy 188 Cobalt-base Alloy UDIMET® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000°F (1093°C). The high chromium level coupled with small .. |
|||
Tensile Strength, Yield | 350 - 420 MPa @Strain 0.200 % |
50800 - 60900 psi @Strain 0.200 % |
|
SSAB Tunnplat Aluzink 350A YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Aluzink YP - HSLA steel (aluminum-zinc coated sheet). Property values are for thicknesses 0.4 - 2.0 mm. Iron content is approximate - exact composition is .. |
|||
Tensile Strength, Yield | 350 - 440 MPa @Strain 0.200 % |
50800 - 63800 psi @Strain 0.200 % |
|
SSAB Tunnplat Docol® 350YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Tensile Strength, Yield | 350 - 440 MPa @Strain 0.200 % |
50800 - 63800 psi @Strain 0.200 % |
|
SSAB Tunnplat Docol® 600DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - Extra high-strength steel (EHS). Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact.. |
|||
Tensile Strength, Yield | 350 - 420 MPa @Strain 0.200 % |
50800 - 60900 psi @Strain 0.200 % |
|
SSAB Tunnplat Dogal 350YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Dogal YP - HSLA steel. Property values are for thicknesses 0.4 to 2.5 mm. Iron content is approximate - exact composition is not reported by the manufactur.. |
|||
Tensile Strength, Yield | 350 MPa | 50800 psi | |
SSAB Tunnplat Domex® 024 BOR Rolled Boron Steel Domex® is the brand name of hot rolled products from SSAB Tunnplat. Compared to conventional quenched and tempered steels, boron steel have several benefits including better formability. Boron .. |
|||
Tensile Strength, Yield | >= 350 MPa | >= 50800 psi | |
SSAB Tunnplat Domex® 350XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. Gene.. |
|||
Tensile Strength, Yield | >= 350 MPa | >= 50800 psi | |
SSAB Tunnplat Domex® 350YP Cold-forming Steel, HSLA Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. General use of Domex®.. |
|||
Tensile Strength, Yield | >= 350 MPa @Strain 0.200 % |
>= 50800 psi @Strain 0.200 % |
|
CLAL-MSX NICLAL 1300 H12 1/2 Hard Copper Alloy, Free Cutting Nickel-Silver Main Characteristics: Good ductilityGood corrosion resistanceTypical Applications:High volume turned partsKeysInformation provided by CLAL-MSX |
|||
Tensile Strength, Yield | 350 MPa @Temperature 700 °C |
50800 psi @Temperature 1290 °F |
R<sub>p</sub>02 |
Assab Steels QRO 90 SUPREME Hot Work Steel QRO 90 SUPREME is a high-performance, chromium-molybdenum-vanadium alloyed hot-work tool steel which is characterized by: Excellent high temperature strength and hot hardnessVery good temper resista.. |
|||
Tensile Strength, Yield | 350 - 550 MPa | 50800 - 79800 psi | before hot stamping |
ArcelorMittal Usibor® 1500 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Yield | 350 - 550 MPa | 50800 - 79800 psi | before hot stamping |
ArcelorMittal Usibor® 1500 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Yield | 350 MPa | 50800 psi | |
AK Steel DI-MAX® HF-10 Nonoriented Electrical Steel DI-MAX HF-10 is a fully processed nonoriented electrical steel designed for use in high speed motors, traction motors, aircraft generators, and other rotating equipment operating at frequencies abov.. |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 % |
50800 psi @Strain 0.200 % |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 % |
50800 psi @Strain 0.200 % |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Tensile Strength, Yield | 350 MPa @Strain 0.200 % |
50800 psi @Strain 0.200 % |
|
Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |