Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 34.5 MPa | 5000 psi | 2 in per min, tangent; ASTM D638 |
Network Polymers NPP 30-3500 NA Description: Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 34.5 MPa @Thickness 3.20 mm |
5000 psi @Thickness 0.126 in |
At 51mm/min, injection molded ASTM Type 1 specimen; ASTM D638 |
Pinnacle Polymers 1112 Polypropylene Homopolymer, Injection Molding Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an.. |
|||
Tensile Strength, Yield | 34.5 - 46.9 MPa | 5000 - 6800 psi | Average value: 42.1 MPa Grade Count:3 |
Overview of materials for Polyphenylene Ether, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Impact Grade". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
M. Holland Company AB308LG ABS Acrylonitrile Butadiene Styrene High flowGood impact resistanceHigh stiffnessApplications: Household goodsPackagingInformation provided by M. Holland |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Techmer ES HiFill FR® ABS GB10 FR 10% Glass Bead Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 10% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Techmer ES HiFill® HDPE GF15 BK 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Spartech PE4325 Reinforced High Density Polyethylene Compound Spartech Polycom's filled high molecular weight, high density polyethylenes are specifically designed for blow molding and sheet extrusion /thermoforming of structural parts. These materials offer a.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D 638 |
Styrolution PS 1900 GPPS Foam extrusionVery high flowHigh heat resistanceFree of zinc and oil additivesInformation provided by Styrolution |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Techmer ES HiFill FR® PP GF10 FR BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightFeatures: Flame Retardant Appearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Techmer ES HiFill® HDPE GF15 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3488-01 is a specially formulated homopolymer polypropylene designed for large appliance injection molding. This material has excellent chemical resistance in addition t.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ISO 527-2 |
Borealis HB300TF Polypropylene HB300TF is a polypropylene homopolymer intended for thermoformed packaging applications. This grade is produced using the Borealis nucleating technology. Its increased crystallization temperature a.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3488-01 is a specially formulated homopolymer polypropylene designed for large appliance injection molding. This material has excellent chemical resistance in addition t.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3490-01G Natural is a homopolymer for extrusion and compounding applications. This material can also be used as a carrier resin for color concentrates. ApplicationPP 349.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene DescriptionPolypropylene PP 1255-01 Natural is a general purpose molding grade, with UL 94 HB approval, homopolymer polypropylene. ApplicationPolypropylene PP 1255-01 meets FDA Regulation 21 CFR 177.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 829-01 is a homopolymer polypropylene approved to Ford specification ESB-M4D63A. Primarily used for interior automotive components, this material is also well suited for.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Washington Penn Homopolymer Polypropylene 50% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 3489-01 Polypropylene Homopolymer DescriptionPolypropylene PP 3489-01 is a specially designed homopolymer with excellent stiffness properties. ApplicationTypical applications include high speed extrusion, high speed thin wall injec.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3490-01G Natural is a homopolymer for extrusion and compounding applications. This material can also be used as a carrier resin for color concentrates. ApplicationPP 349.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Eastman Tenite 350A4861313 Cellulose Acetate Propionate, Clear, Trsp Applications:Blood TherapyDrug DeliveryIV ComponentsMedical DevicesSurgical InstrumentsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughne.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | chs 50 mm/min; tangent; ASTM D638 |
Diamond Polymers NPP30-3500F Homopolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Clariant Renol 6601FR Nylon 66, Flame Retardant Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | 2 in/min; D-638 |
Bapolene® 4042 Polypropylene, Fiber/Filament Grade Bapolene PP4042 is a fiber extrusion resin with excellent thermal and mechanical properties. This product meets FDA standards for food contact applications.Applications: Rope and twine, fibrillated.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3488-01 is a specially formulated homopolymer polypropylene designed for large appliance injection molding. This material has excellent chemical resistance in addition t.. |
|||
Tensile Strength, Yield | 34.5 MPa | 5000 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® 1102KR Cast Film Polypropylene HomopolymerApplications: Cast film applications such as slit tape fabric stock and cordage.Formolene 1102KR is a highly isotactic polypropylene homopolymer designed primarily for cast film applicati.. |