Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 325 MPa @Strain 0.200 % |
47100 psi @Strain 0.200 % |
|
Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Tensile Strength, Yield | 325 MPa @Strain 0.200 %, Temperature 870 °C |
47100 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 325 MPa @Strain 0.200 %, Temperature 205 °C |
47100 psi @Strain 0.200 %, Temperature 401 °F |
|
Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Tensile Strength, Yield | 325 - 385 MPa | 47100 - 55800 psi | |
ArcelorMittal HSLA 320 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S315MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Tensile Strength, Yield | 325 MPa @Strain 0.200 % |
47100 psi @Strain 0.200 % |
|
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |