Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir RT 461F Polystyrene High impact, heat resistant polystyrene with good stiffness. Recommended for improving the thermal performance of injection moulded technical parts which are submitted to high temperature in service.. |
|||
Tensile Strength, Yield | 32.0 - 36.0 MPa | 4640 - 5220 psi | |
Reliance Industries Polypropylene Homopolymer Typical properties of Reliance - Repol Polypropylene gradesInformation provided by Reliance Industries |
|||
Tensile Strength, Yield | 32.0 MPa @Temperature 100 °C |
4640 psi @Temperature 212 °F |
ISO 527 |
Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded
(discontinued **) AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistan.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
North Wood Plastics Polypropylene with 20% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ABL12 ABS LNP* Lubricomp* ABL12 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% Glass Bead and 5% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638-02 |
Ipiranga Petrochem GF 4960 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ AA36H Polypropylene Homopolymer Description: Hifaxâ„¢ AA36H conventional melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processabi.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS LNP* STAT-LOY A3000T is a compound based on ABS. Added features of this grade include: Antistatic, Clear. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527 |
Styrolution Terblend® N NMX04 ABS/PA6 (Conditioned) Terblend N NMX04 is an ABS/PA6 blend specially developed for painted exterior applications, combining impact resistance with excellent processability and paintability.Information provided by STYROLU.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Tipco Tipcolene® FPT 30 PPC - 30% Talc Reinforced Polypropylene Copolymer Compound 30% Talc Reinforced PP CopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Tisan TISOPLEN® 30% Talc Filled Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PPH 9059 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9059 is homopolymer.ApplicationATOFINA Polypropylene PPH 9059 is intended for extrusion of bulk continuous filament (BCF) and continuous filament (CF) fibers. PPH 9059 has.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PPM H350 Polypropylene, Homopolymer Medical Grade Polypropylene PPM H350 is a homopolymer with a Melt Flow Index of 35 g/10 min recommended for the manufacture of medical packaging and medical devices, to the exclusion of implants.Polypropylene PPM.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PSI 3630 Medium Impact Polystyrene 3630 is an easy flowing, medium impact polystyrene for injection molding. This grade offers a good compromise of flow and softening point allowing for the production of large and complex articles a.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene DescriptionPolyfort® FPP 3443U is a 40% talc fortified UV resistant homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min, 4 mm; ISO 527 |
Chi Mei Kibiton® PB-5925 SBC Transparency, high stiffness, injection grade |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Braskem H 301 Injection Molding Polypropylene Description: H 301 is a high melt flow rate homopolymer designed for injection moulding and fiber extrusion. This product exhibits excellent processability with good melt strength and stiffness/impa.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336M30L Mica Reinforced |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336W30L Wollastonite Reinforced |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339C10L1 Calcium Reinforced |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339W30L1 Wollastonite Reinforced |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Carmel Olefins CAPILENE® T 50 Polypropylene Homopolymer CAPILENE® T 50 is a high melt flow rate homopolymer for injection molding characterized by good flow properties combined with good stiffness. APPLICATIONS CAPILENE ® T 50 is recommended for in.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | |
BASF Polystyrol® 585 K Impact Grade Polystyrene (Europe) Special high gloss, high-impact grade for all types of housings. Basis product for gloss capping.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | |
TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Fumed Silica - Wacker HK N20 MILLATHANE E34 is a high performance polyether polyurethane rubber for applications requiring: high abrasion resistance, low temperature flexibility, ozone resistance, oil and fuel resistance, outst.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min |
Eastman Tenite 383A-12 CAP Cellulose Acetate Propionate
(discontinued **) 12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
BP Amoco Acclear® 8449 Random Copolymer Polypropylene, High Clarity Grade
(discontinued **) Suggested fabrication methods: Injection molding; Stretch blow moldingFeatures: Ultra high clarity, Good impact, Excellent static controlTypical applications: Housewares, Rigid packagingComplies wit.. |