Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 31.0 MPa | 4500 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Syncure™ System S107FH Polyethylene, Crosslinked (XLPE) UL Bullentinized, silane-grafted (2-step) moisture crosslinkable polyethylene system, UL 90°C.NOTE: The above represents Typical Properties measured on 18 AWG with 30 mil wall. STORAGE AND HANDLING.. |
|||
Tensile Strength, Yield | 31.0 - 42.7 MPa | 4500 - 6200 psi | Average value: 37.3 MPa Grade Count:22 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Sheet This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Sheet". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
LyondellBasell Lupolen® 6031 M HDPE, Injection Molding Grade Easy flow, injection molding grade for fruit crates, tote boxes and bottle crates, cartridges, protective headgear, buckets, dishes, cartridges for adhesive film canisters, aerosol lids, child seats.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
Flint Hills P5M6K-080 Polypropylene Random Copolymer Features: Clarified, Gamma Radiation Sterilizable. Product does not contain animal derived components. Phthalate-free.Applications: Injection molding: Disposable Syringes. This product is not rec.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
LG Chemical LUPOL GP-1000FA General Purpose Polypropylene, High Impact, Flame Retardant, Non-Bleed LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | 2 in/min (50 mm/min); ASTM D-638 |
Ineos J60-1700-173 HDPE J60-1700-173 is a high density polyethylene homopolymer. This resin is a product of Ineos' technology and is characterized by a narrow molecular weight distribution. Parts fabricated from this mater.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | 2 in/min (50 mm/min); ASTM D-638 |
Ineos T60-800 HDPE Ineos T60-800 is a high density polyethylene homopolymer. This narrow molecular weight distribution resin is a product of Ineos' innovative technology. Parts fabricated from this material exhibit .. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ML004S PP LNP* LUBRICOMP* ML004S is a compound based on Polypropylene resin containing 20% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
Techmer ES Electrablend® HIPS Availability: North AmericaForms: PelletsFeatures: ConductiveInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
Techmer ES HiFill® HDPE UV Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
A. Schulman PP 3479-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 3479-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding .. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
A. Schulman PP 3479-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 3479-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding .. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
A. Schulman POLYFORT™ FPP 1842 Homopolymer Polypropylene DescriptionPolyfort® FPP 1842 is a high stiffness, high heat resistant filled homopolymer polypropylene developed especially for instrument panel clusters. It is opaque to high intensity light.Inf.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
Tipco Tipcolene® FPC 10 - 10% Calcium Carbonate Reinforced Polypropylene Homopolymer 10% Calcium Carbonate Filled PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO 572-2 |
Total Lumicene® MR30MX0 Metallocene Random Copolymer Polypropylene, Injection Molding and Injection Blow Molding Lumicene® MR30MX0 is a metallocene random copolymer with a melt flow index of 30 g/10 min for injection and injection stretch blow molding. Lumicene® MR30MX0 differs from the other random copolyme.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1477 Mineral Filled, General-Purpose Polypropylene DescriptionPolyfort® FPP 1477 is a 20% mineral filled, general-purpose polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
Washington Penn PPC3MF1.5-Black Polypropylene, 15% Mica-Filled, Chemically-Coupled Heat Stabilized injection molding compound. Meets physical requirements for General Motors Spec. GMP.PP.024.Applications: HVAC duct and other various automotive applications.Data provided by Washin.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
A. Schulman PP 3471-01 Polypropylene High Flow Homopolymer Polypropylene DescriptionPolypropylene PP 3471-01 is an ultra high flow homopolymer polypropylene designed for high speed, thin wall injection molding.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 4009 Acrylonitrile Butadiene Styrene ABS with high impact resistanceHigh impact resistance at low temperature, high gloss, good processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO 527-1/2 |
CTC X-PRO TF 1120 HP Polypropylene Homopolymer, 20% Talc Filled X-PRO TF 1120 HP is a 20% talc reinforced polypropylene homopolymer, heat stabilized, and made of 98% recycled content. It has applications in: automotive under hood, IP components, fan and lightin.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO 527-1/2 |
CTC X-PRO TF 1140 HP Polypropylene Homopolymer, 40% Talc Filled X-PRO TF 1140 HP is a 40% talc reinforced polypropylene homopolymer, heat stabilized, and made of 98% recycled content. It has applications in: automotive under hood, IP components, HVAC, and lawn .. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | molded and tested in accordance with ASTM D 4101; ASTM D638 |
Dow 5D49 Polypropylene Resin DOW 5D49 is intended for use fiber spinning processes. It is well suited for spunbond non-woven applications.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braske.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DMDA-8904 NT 7 High Density Polyethylene Resin DOW DMDA-8904 NT 7 is produced using UNIPOL™ process technology. It is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. Information.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO R 527 |
Fainplast Compounds MRT 256/G Medical Rigid PVC, Injection Molding Beta and gamma resistant connectors |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334M40CL Mica Reinforced Coupled |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
BASF Procom® X25H 650 Polypropylene Electrical and domestic appliances, housings where high gloss is required.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Benzoflex T-150 Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM-D638 |
Braskem HB0454HR HDPE Blow Molding Polyethylene Copolymer HB0454HR is a high-density polyethylene copolymer resin with average molecular weight produced by the Unipol® process. A bottle made with HB0454HR shows excellent processability, color, and superfi.. |
|||
Tensile Strength, Yield | 31.0 MPa | 4500 psi | TM R050-36 |
Resinlab® EP1306 Acrylic / Epoxy Hybrid Adhesive EP1306 is a two part acrylic / epoxy hybrid adhesive utilizing a 50% weight loading of aluminum powder into both components. It cures quickly at room temperature to a tough, rigid polymer. It has go.. |