Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 305 MPa @Strain 0.200 % |
44200 psi @Strain 0.200 % |
|
Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Tensile Strength, Yield | 305 MPa @Strain 0.200 % |
44200 psi @Strain 0.200 % |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 305 MPa @Strain 0.200 %, Temperature 870 °C |
44200 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
Tensile Strength, Yield | 305 MPa @Strain 0.200 %, Temperature 315 °C |
44200 psi @Strain 0.200 %, Temperature 599 °F |
|
Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |