Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir R 321P Polystyrene Medium impact polystyrene combining easy flow and high stiffness. For injection moulding of parts with low thickness and high rigidity. Designation: Thermoplastics ISO 2897-PS-I,M,083-12-04-30Applic.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 2 in/min, Type IV bar; ASTM D638 |
Chevron Phillips Marlex® C513UV HDPE Blow Molding Resin
(discontinued **) Resin Type: Hexene CopolymerCharacteristics: Outstanding impact resistanceExcellent ESCRExcellent processabilityUV stabilizationApplications: Intermediate bulk containersAgricultural containersInfor.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Flint Hills P6G2Z-090 Impact Copolymer Polypropylene Features: Excellent impact strength and weldability. Product does not contain animal derived components.Applications: Injection Molding and thermoforming - Automotive coolant bottlesInformation p.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527 |
Iran Petrochemical (PCC) EX 5 HM 9450 F High Density Polyethylene EX5 is a high density polyethylene with 1-Butene as co monomer.Applications: film extrusion, counter bag, carrier bag, wrapping filmsInformation provided by Iran Petrochemical Commercial Co. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
LyondellBasell Astryn BC78A Polypropylene Copolymer, 23% Talc Key Features: high melt flow, high modulus, mineral-filled polypropylene copolymer, high rigidity, good colorability, good processabilityApplications: automotive interior trim components, pillar mol.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP FX04491H PE LNP LUBRICOMP* FX04491H is a compound based on Polyethylene resin containing Proprietary Fillers. Added features of this material include: Wear Resistant. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON CX99000 PS (Europe-Africa-Middle East) LNP* STAT-KON* CX99000 is a compound based on Polystyrene containing Carbon Powder. Added features include : Electrically Conductive, Easy Molding. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon TD000 LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON TD000 PU LNP* STAT-KON* TD000 is an unfilled compound based on Polyurethane resin. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ISO 527-2 |
Borealis BB125MO Polypropylene Copolymer BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow molding and sheet extrusion, and features extremely good process ability with improved melt strength a.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ISO 527-2 |
Borealis BL1481 High Density Polyethylene BL1481 is a semi high molecular weight polyethylene comprising an extra ordinary ESCR and very good chemical resistance This product is intended for blow molding. This grade is available in granular.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 3454F Talc Filled Copolymer DescriptionPolyfort® FPP 3454F is a 20% talc filled copolymer.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene DescriptionPolypropylene PP 2175 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
Total PPC 3666 Polypropylene, Heterophasic Copolymer, Extrusion Polypropylene PPC 3666 is a heterophasic copolymer with a Melt Flow index of 1.5 g/10 min. This resin offers an outstanding processability in combination with good melt strength and excellent mecha.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene DescriptionPolyfort® FPP 1245U is a 20% CAC03 filled UV stable copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene DescriptionPolypropylene PP 2175 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
Borealis BorSafe™ HE3490-IM HDPE Compound for Injection Molded Pressure Fittings BorSafe™ HE3490-IM is a bimodal polyethylene compound produced by the advanced Borstar® technology. Well dispersed carbon black gives outstanding UV resistance. Long term stability is ensured by .. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO R 527 |
Arkema Group OREVAC® 18751 Maleic Anhydride Modified Polypropylene DescriptionOREVAC 18751 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It combines the processability of an extrusion coating resin with the thermal resi.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Aclo Accuguard Polypropylene CP0467V2CSL Copolymer Flame Retardant Copper Stabilized |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min |
Arkema Group Kynar® FLEX 2822 PVDF
(discontinued **) Designation ISO 12086-VDF/HFP-K, EDN, N. ?E5.C.H.B.C,, ? (4-8)Kynar FLEX PVDF are fluorinated thermoplastic copolymers.Outstanding characteristics of Kynar FLEX: chemical resistance, imperviousness .. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527 |
Unipetrol PP MONSTEN® FC 908 Polypropylene Random Copolymer Applications include injection molding and packaging films. Slip and antiblocking agent stabilization. Random copolymer.Information provided by Unipetrol RPA |
|||
Tensile Strength, Yield | >= 24.0 MPa | >= 3480 psi | ASTM D638 |
Buckeye Polymers BP RPP 4008 TR BLK Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |