Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D412 |
Precision Polymer Engineering Z85B Hydrogenated NBR Compound Peroxide cured, Hydrogenated Nitrile Rubber, 76-85 °IRHD. Medium acrylonitrile content (ACN =36%). ASTM designation = HNBR. ASTM D2000 line call-out MDH814, A26, B36, EO16, EO36, F14.Applications.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | 2in (50mm) per min.; ASTM D638 Type 4 |
Polymer Industries Densetec HDPE Pipe Grade The material displays improved performance characteristics in a variety of piping applications. In addition the material is UV stabilized and ideal for use in demanding outdoor applications. It reta.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
Ineos Nova 5751 High Impact Polystyrene
(discontinued **) High flow, Good impact, USP Class VIApplications: Single service impact, Medical, Housewares, CompoundingProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwi.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | 2 in/min, Type IV bar; ASTM D638 |
Chevron Phillips Marlex® HHM TR-480X HDPE Pipe and Corrugated Extrusion Resin
(discontinued **) Characteristics: Good long-term hoop strength performanceVery high melt strengthOutstanding low temperature toughnessApplications: Municipal, industrial, and mining pipeOil and gas gathering pipeInf.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman M2004-P Polyethylene
(discontinued **) M2004-P polyethylene is suggested for applications such as spiral-wound can linings, release paper and photographic paper. M2004-P has been found to exhibit good barrier properties, temperature res.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
Chevron Phillips Marlex® HMN 4550 Polyethylene, Injection Molding Grade, HDPE
(discontinued **) Meets FDA Regulation 177.1520. High stress crack resistance, impact strength, and warpage resistance.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 7550 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527-1,-2 |
Inno-Comp INNOPOL® CS 2-3302 Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-3302 is an elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-3302 is developed for produ.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638-64T |
Micropol Microlin ML27 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited |
|||
Tensile Strength, Yield | 22.0 - 28.0 MPa | 3190 - 4060 psi | ASTM D638 |
Solvay Specialty Polymers solvene® T 2808 Electroactive Polymer (EAP) Annealing Temperature - < 135 °C; Breakdown Voltage - 250 kV/mm; Coercive Field - 50 kV/mm; Crystallization Point - ASTM D3418 123 °C; Curie Temperature - ASTM D3418 110 °C; d33 - -38.0 pC/.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX05305C PC (Asia Pacific) LNP* Stat-kon* DX05305C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | Crosshead speed 100 mm/min; ISO 527 |
SCG Chemicals EL-Leneâ„¢ H5211PC High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good balance of MRS, SCG, and RCPRecommended Applications: Water pressure and gas pipesCertification: Certified by EXOVA, LNE, AENOR,.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | At 50 mm/min; ISO 527-2 |
Borealis Borstar® HE3470-LS Black HDPE Compound for Pressure Pipes Borstar HE3470-LS is a black, high density polyethylene compound classified as an MRS 8.0 material (PE80) produced by the advanced Borstar technology. Well dispersed carbon black gives outstanding .. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
Unipetrol PE HD LITEN® MB/ML 67 HDPE Made for injection molding applications.Information provided by Unipetrol RPA |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene DescriptionLP 642 is a narrow molecular weight copolymer, high-density polyethylene combining high flow for thin wall articles with excellent toughness. ApplicationApplications of LP 642 include fo.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
Tipco Tipcolene® PPC FR V0 - UL94-V0 Flame Retardant Polypropylene Copolymer V-0 Flame Retardant PP CopolymerApplications: Electrical & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D 638 |
Cossa Polimeri ESTASTIR HI 0412 Polystyrene Polystyrene for injection molding or extrusionHigh impact resistance, good thermal resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | 2 in/min, Type IV bar; ASTM D638 |
Chevron Phillips Marlex® 9398 HDPE Pipe and Corrugated Extrusion Resin Resin Type: Hexene CopolymerCharacteristics: Good melt strengthExcellent ESCRApplications: ConduitDuctInformation provided by Chevron Phillips. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436C10L Calcium Reinforced |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | Typical; ISO 527-1/2 |
Axion Polymers Axpoly® PS01 3009 Green General Purpose Polystyrene PS01 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS01 range of resin co.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437G5M25CL Glass/Mineral Reinforced Coupled |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO R 527 |
Addiplast Addilene J 370 Polypropylene Copolymer High impact strength, high elongation at breakInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 22.0 MPa @Temperature 80.0 °C |
3190 psi @Temperature 176 °F |
ISO Data |
BASF Ultraform N 2640 Z4 UNC Q600 POM Ultraform N2640 Z4 UNC Q600 is a high toughness, elastomer-modified injection molding POM grade. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
A.D. Compound Adene NCFAG Copolymer 20% CaCO3 Filled Polypropylene Information provided by A.D. Compound |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
A.D. Compound Adene NTFAG Copolymer 20% Talc Filled Polypropylene Information provided by A.D. Compound |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527-2 |
Arkema Group OREVAC® CA 100 Grafted Maleic Anhydride Polypropylene OREVAC® CA 100 is a chemically functionalized polypropylene with a high content of maleic anhydride. Grafting on polypropylene backbone is achieved with a processing technology which allows to opti.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
ExxonMobil Escorene® HD-8760 LHDPE Rotational Molding Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.HD-8700 series are linear high density polyethylene resins that provide outstanding environmental stress crack resistance. HD-8760 is fully formula.. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene DescriptionPolyflam® RPP 1174 is a high performance talc filled homopolymer polypropylene product with UL V0 flammability and 105°C temperature index at 0.81 mm. RPP 1174 is non-dripping and has .. |
|||
Tensile Strength, Yield | 22.0 MPa | 3190 psi | At 50 mm/min; ISO 527-2 |
Borealis Bormed™ HE7541-PH HDPE for Healthcare Applications Bormed HE7541-PH is a bimodal, natural, high-density polyethylene produced by the Borstar PE technology. Bormed HE7541-PH combines low volatiles with high Environmental Stress Crack Resistance (ESC.. |