Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Nylene® PA6/6 Glass Filled 5133 HS Nylon 6/6 33% Glass Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Oxford Polymers Oxnilon 66-50GF 50% Glass Fiber Filled Nylon 66 for Injection Molding 50% Glass Fiber Filled Nylon 66 for Injection MoldingInformation provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Polymer Resources NY66-G43-[color]-H Nylon 66, 43% Glass Reinforced, Heat Stabilized Nylon 66, 43% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Polymer Resources NY66-G43-[color]H Nylon, 43% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | Conditioned; ISO 527-2 |
Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA)
(Unverified Data**) Ixef 1622 is an impact modified, 50% glass-fiber reinforced polyarylamide. which exhibits very high strength and rigidity, outstanding surface gloss, and excellent impact resistance. - Natural: Ixef.. |
|||
Tensile Strength, Yield | 200 - 380 MPa | 29000 - 55100 psi | |
Materion Beryllium Copper Alloy 25 Strip; A -Planished (TB00) Temper (UNS C17200) Treatment required for max strength: as suppliedFormability Ratio, 90° Bend, Radius/Thickness (Good Way): 0Formability Ratio (bad Way): 0Superficial Hardness: 30T 46-67Tabulated properties apply .. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | |
Kinetics MIM 316 Stainless Steel (Standard Grade) Austenitic stainless steel. Excellent corrosion resistance. Non-magnetic. Lower cost, elongation, and ductility than “premium†grade. Often used for food industry, marine, medical, and app.. |
|||
Tensile Strength, Yield | 200 MPa @Strain 0.200 %, Temperature 871 °C |
29000 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 200 MPa @Strain 0.200 %, Temperature 538 °C |
29000 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Techmer ES HiFill® PA6/12 CF30 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 50% Filler by WeightAppearance: Black and Natural ColorTPCI# 9814104Information provided by TP Composites, .. |
|||
Tensile Strength, Yield | <= 200 MPa @Strain 0.200 %, Thickness <=0.700 mm |
<= 29000 psi @Strain 0.200 %, Thickness <=0.0276 in |
20 MPa higher apply |
SSAB Tunnplat Aluzink F40A Metal-coated Mild Steel Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF43 HS L BK001 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
Tensile Strength, Yield | <= 200 MPa @Strain 0.200 % |
<= 29000 psi @Strain 0.200 % |
|
SSAB Tunnplat Dogal F40 Metal-coated Mild Steel Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Techmer ES Luriblend® PA6 GF40 ML5 HS 12 mm 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 40% Filler by WeightAdditive: Heat Stabilized and Molybdenum Disulfide LubricantFeatures: Lubricated and Heat StabilizerAp.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12 LNP* THERMOCOMP* IC006 is a compound based on Nylon 6/12 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006SXZ PA 66 LNP* THERMOCOMP* RF006SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Heat Stabilized. |
|||
Tensile Strength, Yield | >= 200 MPa | >= 29000 psi | Recommendation only |
SSAB Tunnplat Domex® 200 Cold-forming Steel Cold-forming SteelCharacteristics: Domex® is specifically intended for deep-drawing operations. Due to its close tolerances and fine surfaces, hot-rolled Domex 200 can replace cold reduced deep-.. |
|||
Tensile Strength, Yield | >= 200 MPa @Strain 0.200 % |
>= 29000 psi @Strain 0.200 % |
|
Schmolz + Bickenbach UGICHROM 4404 Austenitic Chrome Plated Bar Description: Ugichrom combines the high efficiency of micro-fissuring chromium plating with the technology of Ugitech’s most advanced gradesAdvantages: Zero defects guarantee; Low friction coef.. |
|||
Tensile Strength, Yield | >= 200 MPa @Strain 0.200 % |
>= 29000 psi @Strain 0.200 % |
|
Schmolz + Bickenbach UGICHROM 4571 Austenitic Chrome Plated Bar Description: Ugichrom combines the high efficiency of micro-fissuring chromium plating with the technology of Ugitech’s most advanced gradesAdvantages: Zero defects guarantee; Low friction coef.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
E-Polymers TEKAMID® TB120G45 , 45% Glass Fiber Reinforced PA6, DAM 45% Glass Fiber Reinforced, High Strength.Information provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 200 MPa @Strain 0.200 %, Temperature 371 °C |
29000 psi @Strain 0.200 %, Temperature 700 °F |
|
Carpenter 20-Mo6® Stainless Steel, Tensile Properties at 93°C Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, .. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Conditioned) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® KR 4355 G7 BK 00564 35% Glass Filled PA6/6T (Conditioned) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r.. |
|||
Tensile Strength, Yield | 200 MPa @Strain 0.200 %, Temperature 538 °C |
29000 psi @Strain 0.200 %, Temperature 1000 °F |
|
AK Steel 309 Austenitic Stainless steel AK Steel 309 provides excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures. The alloy is non-magnetic as annealed and becomes slightly magnetic wh.. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | |
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Bake Hardenable (BH 250) Information provided by AK Steel |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | |
Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.0 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i.. |
|||
Tensile Strength, Yield | >= 200 MPa | >= 29000 psi | Guaranteed Minimum L-T Direction; 0.2% Offset |
Aleris HOGAL 5558 Aluminum 5026 H14/H34 HOGAL 5558 is produced according to EN AW-5026.Information provided by Aleris. |
|||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
Asahi Kasei Thermylon® NSG-240A-2H 50% Ceramic and Glass Fiber Reinforced Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 200 MPa @Strain 0.200 %, Temperature 760 °C |
29000 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |