- Polymer Property : Tensile Strength, Yield = 2600 psi
Polymer Property : Tensile Strength, Yield = 2600 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable 1800-xx19D Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W2407L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W9400 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Iceberg Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| LyondellBasell Petrothene® GA837091 Linear Medium Density Polyethylene ApplicationsPETROTHENE GA 837-091 is a broad molecular weight, medium density resin designed for extrusion and injection-blow molding. An antioxidant had been added to ensure thermal stability. Pro.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| Lubrizol Hipscon™ M-505 Static Control High Impact Polystyrene Hipscon™ M-505 is a conductive, carbon black filled, High Impact Polystyrene available as extruded sheet. Thermoformed trays are lightweight and easily formed into deep pockets that maintain unifo.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | At 50 mm/min; ASTM D683 IV |
| Borealis Borecene™ RM8342RC Linear Polyethylene for Rotational Molding Borecene RM8342RC is a third generation linear medium density natural polyethylene for rotational molding. Borecene RM8342RC is a special grade, which has passed many rigorous tests and can be cons.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | At 50 mm/min; ASTM D683 IV |
| Borealis Borecene™ RM8343 Linear Polyethylene for Rotational Molding Borecene RM8343 is a third generation linear medium density natural polyethylene for rotational molding. The narrow molecular weight distribution imparted through metallocene catalyst technology pro.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | at max load, 2 in/min; ASTM D638 |
| A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene DescriptionPolyfort® FPP 3391 is a chemically coupled, mineral reinforced high impact resistant, modified polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| A. Schulman PP 1692 Polypropylene High Impact Copolymer DescriptionPolypropylene PP 1692 is an exceptional high impact copolymer with high flow for appearance parts.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | at max load, 2 in/min; ASTM D638 |
| A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene DescriptionPolyfort® FPP 3391 is a chemically coupled, mineral reinforced high impact resistant, modified polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| A. Schulman PP 1692 Polypropylene High Impact Copolymer DescriptionPolypropylene PP 1692 is an exceptional high impact copolymer with high flow for appearance parts.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | |
| TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Black Sulfur Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
| Tensile Strength, Yield | 17.93 MPa | 2600 psi | 2.0 in/min; ASTM D638 |
| ExxonMobil LL 8460.29 Rotational Molding Resin Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance o.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2.0 in/min; ASTM D638 |
| ExxonMobil LLDPE LLP 8450.31 Linear Low Density Polyethylene Resin Product Description: LL 8450 is a linear low density hexene copolymer designed to offer excellent stiffness, processability, whiteness and ESCR. They are ideally suited for applications that require.. |
|||
| Tensile Strength, Yield | 17.93 MPa | 2600 psi | 2.0 in/min; ASTM D638 |
| ExxonMobil LLP8460.29 Rotational Molding Resin Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance o.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D-638 |
| Axiall 8833 Moldings & Extrusions Flexible PVC A clear, flexible PVC compound best suited for 80C automotive tubing applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D-638 |
| Axiall 13872 Wire & Cable Flexible PVC Non-lead stabilized, 720 hour sunlight resistant insulation compound recommended for TW and 75°C Class 43 applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in .. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D-638 |
| Axiall 16930 Wire & Cable Flexible PVC Non-lead stabilized tray cable jacketing compound. UL recognized component for 720 hour sunlight resistance in black only.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation .. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D-638 |
| Axiall 38951 Wire & Cable Flexible PVC Low cost AWM jacket for SPT, SVT, SJT applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D412 |
| Teknor Apex APEX® 3311-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D-638 |
| Axiall 19935 Wire & Cable Flexible PVC THHN-THWN, larger sizes. Microbe resistant.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | |
| TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Black Sulfur Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W2407 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||