Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
Samyang Tripet® 2550GN45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced, Flame Retardant
(discontinue TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information.. |
|||
Tensile Strength, Yield | 157 MPa @Thickness 3.20 mm |
22800 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUMID GP2200B(W) PA66+GF20%, General Purpose Feature: Injection Molding, PA66+GF20%, General PurposeApplication: Automotive PartsCAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific) LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2140 PPS Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced PPS/GS that is used in mobile phone LCD bracketInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced PPS/GS that is used in mobile phone LCD bracketInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL GTX GTX6801 PPE+PA (Asia Pacific) PPE+PA, GF 30% |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ISO 527 |
Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified 33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
Cheng Yu Plastic NG1300S Nylon 66, 30% Glass Fiber Reinforced |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
Ensinger Tecapeek® GF30 Polyetheretherketone, 30% Glass Reinforced (PEEK) Tecapeek™, made from Victrex PEEK polymer, is an excellent material for a wide spectrum of applications where thermal, chemical, and combustion properties are critical to performance. Excellent fle.. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM GF reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
Cheng Yu Plastic FR200GV30 Flame Retardant Nylon 66, 30% Glass Fiber |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | Wet; ASTM D638 |
Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66 43% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Mechanical and electrical parts such as micromotors, automotive parts such as radiator tanks and shift leversInformation provi.. |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | Wet; ASTM D638 |
Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66 Enhanced strength and stiffness; with 33% GF. Superior fluidity and appearance.Applications:Automotive parts Information provided by Asahi Kasei |
|||
Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2140 PPS Information provided by Samsung Cheil Industries. |