Polymer Property : Tensile Strength, Yield = 18400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D638
Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (Cond) Information provided by Ravago.
Tensile Strength, Yield	127 MPa	18400 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL38 PC LNP* Lubricomp* DFL-4038 is a Polycarbonate containing 40% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated.
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D638
LG Chemical LUPOS HR-2307 Heat Resistant SAN, 30% Glass Fiber Reinforced LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have ..
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D638
LG Chemical LUPOY GP-2301F General Purpose Modified PC, 30% Glass Fiber Reinforced, Flame Retardant Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched LNP* LUBRICOMP* OCP36A is a compound based on PPS - Branched resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Electrically Conductive.
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched (Asia Pacific) LNP* Lubricomp* OCL-4536 is a compound based on PPS - Branched resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Internally Lubricated, Electrically Conductive..
Tensile Strength, Yield	127 MPa	18400 psi	SABIC - Japan Method
SABIC Innovative Plastics ULTEM JD7101 PEI (Asia Pacific)
Tensile Strength, Yield	127 MPa	18400 psi	SABIC - Japan Method
SABIC Innovative Plastics Ultem JD7902 PEI (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield	127 MPa	18400 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear LNP* STAT-KON* OCL32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant.
Tensile Strength, Yield	127 MPa	18400 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East) LNP* STAT-LOY* ZF3021 is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic, Flame Retardant.
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Tensile Strength, Yield	127 MPa	18400 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific) PPE+PPS, GF40%, FR V-0
Tensile Strength, Yield	127 MPa	18400 psi	ASTM D638
Ashley Polymers Ashlene® 79MGS Nylon 6, 40% Glass Mineral reinforced A 40% glass mineral reinforced Nylon 6 with good dimensional stability, stiffness, sink and warp resistance. Modified for improved surface appearance.Data provided by the manufacturer
Tensile Strength, Yield	127 MPa	18400 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL APS440 PPE+PPS (Asia Pacific)