Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 108 - 200 MPa | 15700 - 29000 psi | Average value: 133 MPa Grade Count:4 |
Overview of materials for Nylon 612, Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | ASTM D638 |
LG Chemical LUPOY GP-5300 General Purpose PC/ABS Alloy, 30% Polymer Alloy, High Strength, Dimensional Stability Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | ASTM D638 |
Techmer ES HiFill FR® PBT GF30 FR-S AS 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: AntistaticFeatures: Flame Retardant, Antistatic and Non-BloomingProcessing Method: Injection.. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Valox® CS860 PBT+PET (Asia Pacific) 30% glass reinforced PBT+PET blend. Color stable, FR. Housewares, appliances; iron skirt, oven trim/panels.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific) Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | ASTM D638 |
Techmer ES Luriblend® PC CF10 TL15 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: Lubricated and Flame RetardantAppearance: BlackInformation provided.. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL IGN320 PPE+PS 20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL NF1030 PPE+PS (Asia Pacific) |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | At 50 mm/min; ISO 527-2 |
Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced Xmod GD301HP is reinforced with 32% chemically coupled glass fibers and based on specific Polymer matrix material which is bringing excellent mechanical properties (impact behavior) and very good st.. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY 1001 CF20 20% Carbon Fiber Filled ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | ASTM D638 |
Asahi Kasei Thermylene® P-40FG-0860 40% Glass Fiber Reinforced Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | Dry; ASTM D638 |
Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66 15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei |
|||
Tensile Strength, Yield | 108 MPa | 15700 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL CN5246 PPE+PS (Asia Pacific) |