Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 88.9 MPa | 12900 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ MX5210-0040 RS Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Tensile Strength, Yield | 88.9 MPa | 12900 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ PPR-40G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Tensile Strength, Yield | 88.9 MPa | 12900 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ MF 1204 40 Black 13 Polyamide 66 (Nylon 66) The Nymax® MF 1200 Series of mineral-reinforced nylon 6/6 compounds have been specifically engineered to provide an excellent balance of physical property performance, toughness, chemical resistanc.. |
|||
Tensile Strength, Yield | 88.9 MPa | 12900 psi | ASTM D638 |
Omni Plastics OmniTech™ ABS GRC30 NA Glass Reinforced OmniTech™ is a family of non-standard products custom developed for applications with unique functional requirements, including but not limited to: Flame Retardant, Conductive, Wear Resistant, and .. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics LNP COLORCOMP J1000R PES (Europe-Africa-Middle East) LNP* COLORCOMP* J1000R is a compound based on Polyethersulfone resin. Added features include : Mold Release |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics LNP COLORCOMP J1000Z PES (Europe-Africa-Middle East) LNP* COLORCOMP* is a compound based on Polyethersulfone resin. Added features include: High Viscosity |
|||
Tensile Strength, Yield | 89.0 MPa @Temperature 150 °C |
12900 psi @Temperature 302 °F |
ISO 527 |
Solvay Specialty Polymers Amodel® FR-4133 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry as Molded
(d AMODEL FR-4133 is a 33% glass-reinforced polyphthalamide (PPA) resin designed for electrical and electronic applications. This UL94-V0 resin offers the highest mechanical and electrical properties, .. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type 1A, 50 mm/min; ISO 527-2 |
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK) AvaSpire® AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type 1A, 50 mm/min; ISO 527-2 |
Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK) AvaSpire® AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than Ava.. |
|||
Tensile Strength, Yield | 88.9 MPa | 12900 psi | ASTM D638 |
Techmer ES Electrablend® PC SS10 FR BK 10% Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Stainless Steel Fiber, 10% Filler by WeightFeatures: Electromagnetic Shielding (EMI) and Flame RetardantAppearance: BlackInformation pr.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 4521 PBT VALOX 4521 is a high flow, 20% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 4521 PBT (Asia Pacific) 19.5% glass reinforced PBT. High flow, flame retardant. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA 10% Glass Reinforced PPE+PA Alloy. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Europe-Africa-Middle East) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Asia Pacific) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Europe-Africa-Middle East) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA (Asia Pacific) GR 10%. Increased stiffness of 200000 psi (3000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: lighting. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Plain Cast Resin; ASTM D638 |
TSE Industries EcoWIND® P200G High Performance Filament Winding Polyurethane Resin for Pipes TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® re.. |
|||
Tensile Strength, Yield | 88.9 MPa | 12900 psi | ASTM D638 |
Asahi Kasei Thermylene® P6-25FG-0687 25% Glass Fiber Reinforced Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | ISO 527-2/1A/50 |
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 mi.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | Plain Cast Resin; ASTM D638 |
TSE Industries EcoWIND® P200G High Performance Filament Winding Polyurethane Resin for Pipes TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® re.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | ISO 527-2/1A/50 |
Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than AvaSpir.. |
|||
Tensile Strength, Yield | 89.0 MPa | 12900 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s). |