Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50% RH; ISO 527-1 |
Murtfeldt Murytal® H Acetal Homopolymer In addition to the excellent properties of Murytal® C, Murytal® H is stronger and more rigid with a lower expansion coefficient.Special Properties:• High rigidity• Excellent ability to regain it.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® INP562 ABS SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Europe-Africa-Middle East) XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Asia Pacific) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® XHT4143T PC Copolymer (Asia Pacific) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527 |
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES LNP COLORCOMP* JX91550 is an unfilled Polyethersulfone. |
|||
Tensile Strength, Yield | 78.0 MPa @Temperature 23.0 °C |
11300 psi @Temperature 73.4 °F |
ISO 527 |
Victrex® PEEK 450FE20 Polyetheretherketone, 20% PTFE Product Description:High performance thermoplastic material, 20% filled with PTFE Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA foo.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min |
Arkema Group Oroglas® MI-2T Acrylic
(discontinued **) OROGLAS MI-2T is an injection molding acrylic grade that offers excellent thermal resistance with slight improvement in impact performance.Key features improved deformation and toughness : up to 2.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP 9X06483 PA 46 LNP* Lubricomp* 9X06483 is a compound based on a Nylon 4/6 containing PTFE. Added feature of this grade is: Heat Stabilized. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527 type 1 A |
Solvay TECHNYL® C 507XT PA6, DRY Description: Unreinforced polyamide 6, heat stabilized, very high viscosity, for extrusion.Available in: Europe Product Applications: It is suitable for extruded semi-finished products, such as: Rod.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp RL001 PA 66 LNP Lubricomp* RL001 is a Nylon 6/6 base resin containing PTFE lubricant. Characteristics are internally lubricated.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 77.9 MPa | 11300 psi | ASTM D638 |
Techmer ES HiFill® PA6 L BK Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: LubricatedAppearance: BlackTPCI# 9356102Information provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 77.9 MPa | 11300 psi | ASTM D638 |
Techmer ES HiFill® PP GF20 CC HS 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and Chemically CoupledInformation pro.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS LNP* THERMOCOMP* AX04518 is a compound based on ABS resin containing proprietary filler(s). |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DFB03GR PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DFB03GR is a compound based on Polycarbonate resin containing a mixture of Glass Fiber and Glass Beads. Added features of this material include: Easy Molding. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6020 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 mm an.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL PX4716 PPE+HIPS (Asia Pacific) PPE+PS GF15% FR V-1 |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated. |
|||
Tensile Strength, Yield | 77.9 MPa | 11300 psi | ASTM D638 |
Techmer ES HiFill® PP GF20 CC 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightFeatures: Chemically CoupledInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527-1/-2 |
Unitika A1030BRL PA6, Dry Information provided by Unitika Ltd. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527-1/-2 |
Unitika A1030FR PA6, Dry Information provided by Unitika Ltd. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527-1/-2 |
Unitika A1030SR PA6, Dry Information provided by Unitika Ltd. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | GB/1040 |
Zhejiang Juner PA-A7-1 Flame-Retardant & Glass Reinforced, Environmental PA66 Applications: Electric Cabinet BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
Eurostar Starflam P10002Z PA6, Flame Retardant, Extrusion Starflam P10002Z is an Unfilled, Halogen Free, Red Phosphorous Free, Flame Retardant, Polyamide 6 Extrusion ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | dry; ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 MS Polyamide 6 - Natural Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.For uncolored parts produced by injection molding, contain including and demo.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min |
Arkema Group Cristamid® MS 1700 Semi-Aromatic Nylon (PASA) (Dry) Designation ISO 1874-PA12/xx,M,12-020Semi-aromatic polyamide (PASA) grade for injection molding.Transparency even thick. Outstanding thermal properties due to its high glass temperature. Good chemic.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | |
Asahi Kasei Xyron® G701V Modified Polyphenylene Ether Applications: Automotive: Door Handles, Fuse Carriers, Fuse Box Covers, Interior Electrical Outlets, Interior Plugs/Switches, Interior High Precision Parts Electrical and Industrial: Pool and Spa P.. |
|||
Tensile Strength, Yield | 77.9 MPa | 11300 psi | ASTM D638 |
LNP Thermocomp® FP-VC-1003 BK8-019 Polyvinylidene Fluoride, Carbon Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOTUF WF003I Polyester, TP LNP THERMOTUF* WF003I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact. |