Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 708 MPa @Strain 0.200 % |
103000 psi @Strain 0.200 % |
|
Kennametal Stellite Stellite® 6K 1.6 mm thick sheet 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g.. |
|||
Tensile Strength, Yield | 710 MPa @Strain 0.200 %, Temperature 650 °C |
103000 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 80A A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile a.. |
|||
Tensile Strength, Yield | 710 MPa @Strain 0.200 % |
103000 psi @Strain 0.200 % |
|
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
Tensile Strength, Yield | 709 MPa @Strain 0.200 % |
103000 psi @Strain 0.200 % |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Tensile Strength, Yield | 713 MPa @Strain 0.200 % |
103000 psi @Strain 0.200 % |
|
Carpenter Custom 455® Stainless Steel, Annealed, 25 mm Bar Data provided by Carpenter Technology Corporation.Recognizing the need for high-strength alloys with good corrosion resistance to atmospheric environments, the Carpenter Research Laboratory develope.. |
|||
Tensile Strength, Yield | 707 MPa @Treatment Temp. 760 °C, Time 1.44e+7 sec |
103000 psi @Treatment Temp. 1400 °F, Time 4000 hour |
0.2%. Room temp test after thermal exposure |
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
Tensile Strength, Yield | 707 MPa | 103000 psi | |
Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or .. |