Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO value at 50 mm/min. |
BASF Capron® 8202 HS BK-102 Nylon 6 (Dry)
(discontinued **) Capron 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose nylon 6 exhibiting excellent fluidity for filling thin sections. It possesses the combination.. |
|||
Tensile Strength, Yield | 84.0 MPa @Temperature 22.0 °C |
12200 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1500 Unsaturated Polyester UP SMC 1500 is a special SMC for applications calling for high continuous service temperature. The glass level has been selected to combine good mouldability with good strength and stiffness properties.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 LNP* LUBRICOMP* RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific) LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 (Asia Pacific) LNP* Lubricomp* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® 1760E PBT+PC 11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS (Asia Pacific) LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 55/55 with low toxicity, smoke and flame evolution. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | SABIC - Japan Method |
SABIC Innovative Plastics Xenoy® 1760 PBT+PC (Asia Pacific) |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GFN1410V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1410V resin is a blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 10 % glass reinforcement. The resin is suitable for injection molding. Noryl GFN1410V resin has.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D6368 |
Solvay TECHNYL® A 208KBK-10N-L PA66, DRY Description: Polyamide 66, highly UV-resistance, toughness modified for injection molding.Available in: Asia PacificProduct Applications: TECHNYL A 208K BK 10N-L is used in all sectors of industry, .. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
Cresset Powers Cress-Alon™ A2350 2.35 r.v. Injection Molding Grade Nylon 6, Dry As Molded Neat resin, for injection molding.Information provided by Cresset Powers Ltd. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® E51HSB NC010 Nylon 66
(Unverified Data**) Unreinforced Heat Stabilized High Viscosity Polyamide 66 Zytel E51HSB NC010 is a high molecular weight heat stabilized polyamide 66 resin for injection molding and extrusion.Information provided by .. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® EFE1068 NC010T Nylon 66
(Unverified Data**) Unreinforced Polyamide 66Zytel EFE1068 NC010T is a lubricated polyamide 66 for injection molding. It has excellent flow characteristics and was developed for fast production cycles and high producti.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FG53 NC010 Nylon 66
(Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PX05004 PA66, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX05004 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO R527 |
Arkema Group Orgalloy® RS 6010 Polyamide 6 Alloy 10% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | 50mm/min; ISO 527 |
BASF Ultramid® C3U BK23079 PA66/6 (Dry) Ultramid C3U BK23079 is an injection molding, general purpose PA66/6, pigmented black grade with improved flame retardance. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 303 Natural FA PA66, DRY Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe Product Applications: TECHNYL® A 303 Natural FA offers three main advantages: high impact resistanc.. |
|||
Tensile Strength, Yield | 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® E41HSB NC010 Nylon 66
(Unverified Data**) Unreinforced Heat Stabilized High Viscosity Polyamide 66 Zytel E41HSB is an unreinforced high viscosity heat stabilized polyamide 66 for injection molding and extrusion.Information provided by DuPon.. |