Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Nylene® 601 Nylon 6, Extrusion Grade Dry as molded. Extrusion grade. Nylene 601 is the heat stabilized version of 600 which is a general purpose, medium viscosity, extrusion grade resin used in applications such as rods, slabs, and t.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Nylene® NX4569 Nylon 6 Dry as molded. Nylene NX4569 is a medium viscosity, molding grade nylon 6 resin suitable for general purpose applications. Crystallization initiators provide fast molding cycles through rapid melt
.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Nylene® NX5703 Nylon 6, Impact Extrusion Grade Dry as molded. Extrusion grade. Nylene NX5703 is a high residual monomer, medium viscosity resin designed for extrusion applications requiring good flexibility and high strength. NX5703 is ideally.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Nylene® PA6/6 Homopolymer 132 HSL Nylon 6/6 Low Viscosity GP Grade; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Tensile Strength, Yield | 83.0 - 179 MPa | 12000 - 26000 psi | Average value: 101 MPa Grade Count:6 |
Overview of materials for Nylon 66, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Extruded". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, DAM Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by G.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
LG Chemical LUPOY GN-2151F Halogen Free Modified PC, 15% Glass Fiber Reinforced, Flame Retardant, Green Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
LG Chemical LUPOS GP-2200H General Purpose ABS, 20% Glass Fiber Reinforced, High Heat Resistance LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have .. |
|||
Tensile Strength, Yield | 83.0 MPa @Strain 0.200 %, Temperature 980 °C |
12000 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Asia Pacific) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific) LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL NC212 PPE+HIPS (Asia Pacific) |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl PKN4717 PPE+PS (Asia Pacific) PPE+PS. Translucent. FDA compliant. High heat. Foam extrusion. Microwavable. Food packaging uses. Solid properties listed.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6 LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RB008 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RB008 is a compound based on PA 66 resin containing Glass Bead.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Europe-Africa-Middle East) Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FG42L NC010 Nylon 66
(Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
E-Polymers TEKANATE™ G710 , 10% Glass Fiber Reinforced Poly Carbonate 10% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 83.0 MPa @Temperature -40.0 °C |
12000 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8254 HS BK-102 PA6 (Dry) Ultramid 8254 HS is a highly flexible, heat stabilized, impact modified nylon 6 extrusion grade for tubing applications. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® ECO315 BK13 Nylon 66, Flame Retardant, DAM Vydyne® ECO366 BK13 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for m.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Ascend Performance Materials VYDYNE® R220 Nylon, Mineral Reinforced Typical property data. VYDYNE is a registered trademark of Solutia Inc. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 2 in/min; ASTM Test |
BASF Ultramid® NBX-0025 NF2001 PA66 (Dry) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 50mm/min; ISO 527 |
BASF Ultramid® 1000-11 NF2001 PA66 (Dry) Ultramid 1000-11 NF2001 is a general purpose nylon 6/6. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 2 in/min; ASTM Test |
BASF Ultramid® 1000-11 NF2001 PA66 (Dry) Ultramid 1000-11 NF2001 is a general purpose nylon 6/6. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 50mm/min; ISO 527 |
BASF Ultramid® 1000-2 NF2001 PA66 (Dry) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 2 in/min; ASTM Test |
BASF Ultramid® 1000-2 NF2001 PA66 (Dry) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 2 in/min; ASTM Test |
BASF Ultramid® 1003-2 NF2002 PA66 (Dry) Ultramid 1003-2 NF2002 is a general purpose, heat stabilized nylon 6/6. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® ECO366 Nylon 66, Flame-retardant, DAM Vydyne® ECO366 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for machin.. |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
Ashley Polymers Ashlene® 71M Nylon 6, 40% Mineral Filled A 40% mineral reinforced Nylon 6 resin modified for reduced shrinkage.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 83.0 MPa | 12000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP JF002R PES (Europe-Africa-Middle East) LNP* Thermocomp* JF002R is a compound based on Polyethersulfone resin containing Glass Fiber, Glass Bead. Added features of this material include: Mold Release. |