Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
NYCOA 2025 Nylon 6 extrusion and molding grade with mold release and quicker cycle times for sports cleatsInformation provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Nylene® 404 Nylon 6 Injection molding grade. Dry as molded. Nylene 404 is a heat stabilized version of 401 which is recommended for general purpose nylon molding applications in both thin and heavy sections. In additi.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Nilit Polynil® P36 Very High Flow Nylon 66 Description: Very high flowApplication: CompoundingInformation provided by NILIT. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® DMX3415 PC Copolymer Lexan* DMX3415 is a co-polycarbonate resin with improved scratch resistance, high purity and optical quality.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-1/2 |
Radici Radilon® ALX14080 (dry) Nylon 66 Medium high viscosityInformation provided by Radici group. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 5271/2 |
Radici Radilon® S 37FL T Nylon 6 Radilon® S (homopolyamides) are normally used in cast and blown extrusion for the production of packaging films. Radilon® S grades can be extruded to a thickness varying from 20 mm to 100 mm.Appl.. |
|||
Tensile Strength, Yield | 80.0 - 90.0 MPa | 11600 - 13100 psi | Injection; ISO 527 |
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp DFI12E PC LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was suppli.. |
|||
Tensile Strength, Yield | 80.0 MPa @Strain 0.200 %, Temperature 982 °C |
11600 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 402H1 Natural PA66, DRY Description: TECHNYL® A 402H1 is an unreinforced polyamide 66, very high viscosity, heat stabilized, for extrusion and injection molding. This product is available in natural color.Benefits: The .. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A |
Solvay TECHNYL® B 50 H1 PA66/6, DRY Description: TECHNYL® B 50H1 is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilized and is suitable for injection molding. This product is av.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 4012G PBT (Europe-Africa-Middle East) VALOX 4012G is a 10% glass fibre reinforced PBT injection moulding resin with excellent mechanical properties. Applications: connectors. This grade is a 4012 with improved cycle time and ductility. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Techmer ES HiFill® PA6 E HS N Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and Nucleating AgentFeatures: Heat Stabilized and NucleatedProcessing Method: ExtrusionTPCI# 9587102Information provided by TP Comp.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON ZE004 PPO LNP* STAT-KON* ZE004 is a compound based on PPO resin containing 20% Carbon Fiber. Added feature of this grade includes: Electrically Conductive. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Europe-Africa-Middle East) NORYL GFN2 is a standard 20 % glass fibre reinforced material with a HDT/A of 130C according ISO 75. NORYL GFN2 can be used for all applications where a higher modulus is required. NORYL GFN2 is ava.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL IGN5531 PPE+PS Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Europe-Africa-Middle East) Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM-D638 |
Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber 30% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
Eurotec® Tecomid® NA40 NL XA70 PA6.6, unfilled, flame retardant - halogen free (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
Eurotec® Tecomid® NB40 NL E PA 6 lubricated, nucleated Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, Conditioned Vydyne® R515 is general-purpose, 15% glass-fiber reinforced PA66 resin. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 15% Filler by WeightAdditive:Lubricant Features.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | dry; ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 MCS Polyamide 6 - Colored Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.For colored parts produced by injection molding.Tarnamid® has the following .. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
BASF Capron® B73ZP Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | |
BASF Luranyl® KR 2456/3 Polyphenylene Ether + Styrene-Butadiene Blend Heat resistant grade containing halogen-free flame-retardant. Mainly used for functional electronic parts that must meet tough fire-safety legislation.Data was collected by ISO methods and provided.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | DAM; ISO 527 Type 1 A |
Solvay Technyl® A 402 H1 Nylon 66 Unreinforced, very high viscosity, heat stabilized, for extrusion and injection molding. TECHNYL® A 402 H1 offers three main advantages: high impact resistance at low humidity levels, good rigidit.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-1/-2 |
DSM Akulon® K225-KWS Nylon 6 (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |