Polymer Property : Tensile Strength, Yield = 63.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CH6410 PC+ABS (Asia Pacific) CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 101R PC (Europe-Africa-Middle East) LEXAN 101R is a high viscosity multi purpose grade and contains a release agent to ensure easy processing. LEXAN 101R is available in transparent, translucent and opaque colours.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 103R PC (Europe-Africa-Middle East) LEXAN 103R is a high viscosity multi purpose U.V. stabilized grade and contains a release agent to ensure easy processing. LEXAN 103R is available in transparent, translucent and opaque colours.
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U..
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FXD921A PC (Europe-Africa-Middle East) LEXAN FXD921A is a transparent/translucent, medium viscosity, flame retardent grade for light diffusion special effects. Color package may affect performance.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® LI1911R PC (Europe-Africa-Middle East) Low-viscosity multi-purpose grade having low levels of ionics species.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® LUX9136C PC COPOLYMER (Asia Pacific) Lexan* LUX9136C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and..
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® ML7678 PC 17.5 MFR, for small, intricate parts. FDA food contact compliant in limited colors. Enhanced mold release package.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® OQ4120R PC (Europe-Africa-Middle East) Optical grade with UV cut-off up to 400 nm, greater optical purity than standard grades. For needs of sunglass and sunvisor markets. MFR of 25.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® VR2020 PC UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 17.5 MFR, for small, intricate parts. UV stabilized. Internal mold release.This data was supplied by SABIC-..
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® VR2520 PC General purpose polycarbonate with melt flow rate of 8.5.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 144R PC UL rated HB. 200 series recommended when V-2 rating required. MFR 10.5. Internal mold release. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer ..
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® AD4820 PC (Asia Pacific) LEXAN AD4820 is a high viscosity grade exhibiting low dust attraction with a UV cut-off up to 400 nm and greater optical purity than standard resin.
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FXM141R PC (Asia Pacific) FXM141R is a Lexan PC grade in Metallic or Pearlescent effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color ..
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
Chi Mei Wonderloy® PC-175D PC/ABS Alloy (discontinued **) Optical Disk
Tensile Strength, Yield	63.0 - 132 MPa	9140 - 19200 psi	Average value: 95.2 MPa Grade Count:12
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum ..
Tensile Strength, Yield	63.0 MPa	9140 psi	ASTM D638
LG Chemical LUPOL LW-4407 Low Warpage Polypropylene, 40% Glass Fiber/Mineral Filler Reinforced, Heat Resistant LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics PC0703R PC (Asia Pacific) PC0703R resin is a low flow (MFR = 7 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the extrusion market.
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics PC0800 PC PC0800 resin is a low flow (MFR = 8 at 300ÂºC/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release.T..
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics PC2203R PC PC2203R resin is a high flow (MFR = 22 at 300ÂºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was suppli..
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm.
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® ENH2900 PBT+PC (Asia Pacific) Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applic..
Tensile Strength, Yield	63.0 MPa	9140 psi	5 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® X4870HH PC+PET Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st..
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL EN265 PPE+PS Extrusion grade. 254F (123C) DTUL. UL94 V-1 rated.
Tensile Strength, Yield	63.0 MPa	9140 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL N1050 PPE+HIPS (Asia Pacific) Noryl* N1050 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR ad..
Tensile Strength, Yield	63.0 MPa	9140 psi
Covestro Makrolon® 3103 Polycarbonate Injection molding and extrusion grade with high viscosity, UV stabilized, special grade for sheets.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Baye..
Tensile Strength, Yield	63.0 MPa	9140 psi
Covestro Makrolon® 6870 Polycarbonate Pseudoplastic behavior and high viscosity extrusion and injection molding grade, less resistant to UV than e.g. MAKROLON 6555.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScie..
Tensile Strength, Yield	63.0 MPa	9140 psi	50mm/min; ISO 527
BASF Ultraform W 2320 003 BK120 Q600 POM Ultraform W 2320 003 BK120 Q600 is a pigmented black, very easy flowing and rapidly solidifying injection molding POM grade for use where processing is extremely difficult but mechanical properties ..
Tensile Strength, Yield	63.0 MPa	9140 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 953A PC (Europe-Africa-Middle East) LEXAN 953A is a high viscosity flame retardant, UV-stabilized grade, especially suitable for electrical applications.