Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
NYCOA 1838 Copolymer Nylon Alloy good impact resistant molding and extrusion gradeInformation provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® INP564 ABS+SAN SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CU1650 PC+ABS (Asia Pacific) UV stabilized, non-FR PC/ABS of excellent flow and impact performance |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CY9650 PC+ABS (Europe-Africa-Middle East) PC+ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat AgingThis data was supplied by SABIC-IP for the Europe-Africa-Middle East re.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS (Asia Pacific) PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCY620HS PC+ABS PC+ ABS General Purpose Non-FR |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY FXW749SK ASA Sparkle VisualFx ASA Resin - Weatherable |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® BFL4000U PC (Europe-Africa-Middle East) Lexan* BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed fo.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL5689 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL5689 polycarbonate (PC) resin is a GF reinforced, UV stabilized, flame retardant injection molding copolymer blend. This medium flow resin features UL94 V0 @ 1.5mm flame retardancy based .. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML7667 PC Copolymer (Asia Pacific) Lexan* ML7667 specialty polycarbonate (PC) resin is a 9% GF reinforced, UV stabilized, flame retarded injection molding grade. This medium flow specialty PC resin combines UL94 V0 @ 1.5mm, 5VB @ 3.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DL002PC PC LNP* LUBRICOMP* DL002PC is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this grade are: Wear Resistant, Exceptional Processing, Clean Compound System. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 |
Eastman 9921P PET Injection Molded
(discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4472 PC (Europe-Africa-Middle East) Lexan* HFD4472 is a 20% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4472 has enhanced mold release, impact ductili.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
LG Chemical Lupox® SV-1120 General Purpose PBT, Unreinforced, High Molecular Weight, Extrusion LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
Tensile Strength, Yield | 54.0 MPa @Strain 0.200 %, Temperature 980 °C |
7830 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific) LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON ZE004 PPO LNP* STAT-KON* ZE004 is a compound based on PPO resin containing 20% Carbon Fiber. Added feature of this grade includes: Electrically Conductive. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp C7410 PC+ABS (Asia Pacific) LNP* Thermocomp* C7410 compound is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 type 1 A |
Solvay TECHNYL® C 536XT PA6, DRY Description: TECHNYL® C 536XT is an unreinforced polyamide 6, high viscosity, for extrusion blow molding. This product is available in natural color.Benefits: The product offers a good processing.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 151 NC010 Nylon 612
(Unverified Data**) Unreinforced Polyamide 612Information provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
Aclo Accutech ABS ABS834G20L Glass Reinforced |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50mm/min; ISO 527 |
BASF Ultramid® 1000-11 NF2001 PA66 (Conditioned) Ultramid 1000-11 NF2001 is a general purpose nylon 6/6. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50mm/min; ISO 527 |
BASF Ultramid® 1000-2 NF2001 PA66 (Conditioned) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
Ashley Polymers Ashlene® RH190TB Acetal Impact modified reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity, black.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FG151L NC010 Nylon 612
(Unverified Data**) Unreinforced Polyamide 612 with Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 54.0 - 58.0 MPa | 7830 - 8410 psi | Average value: 56.3 MPa Grade Count:5 |
Overview of materials for Polycarbonate/ABS Alloy, Antistat/Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Antistat/Conductive". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527-1/-2 |
Unitika EX-1020K PA6, Dry Conducting nylonInformation provided by Unitika Ltd. |
|||
Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min |
Polimeri Europa KOBLEND PCA 51 PC+ABS
(discontinued **) Symbol according to ISO 1043/1: PC+ABS Injection moulding grade with flame retardant properties ( UL 94 V-0 at 1.6mm thickness ) and good light resistance. Vicat/B50 = 90°C Main application field.. |