Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY FXW749SK ASA Sparkle VisualFx ASA Resin - Weatherable |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
RedEye On Demand Polycarbonate High Impact Strength & Temperature Resistant for Rapid Prototyping Polycarbonate (PC) is an actual industrial-grade thermoplastic that is impact-resistant and structurally strong. PC parts are built with a layered manufacturing process utilizing Fused Deposition Mo.. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML7647K PC (Asia Pacific) Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque only |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | |
Ineos ABS Lustran® QE 1045 A, Injection Grade
(discontinued **) Injection molding grade, high modulus, only available in black.Applications: For automotive application.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed.. |
|||
Tensile Strength, Yield | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
LG Chemical LG704W ABS, Low Gloss, Heat Resistance Feature: Injection Molding, Low Gloss, Heat ResistanceApplication: Automobiles Interior Housing (Column Cover, Filllar Etc)CAS No. 25120-20-1, 9003-56-9 and 25747-74-7Information provided by LG Chem.. |
|||
Tensile Strength, Yield | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® GP1000W PBT Description: Injection Molding, PBT, Anti-HydrolysisApplication: IT/OA, Automotive (Connector)CAS No. 24968-12-5Information provided by LG Chemical |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
LG Chemical RS-650 ABS, Extrusion, General Purpose Information Provided by LG Chem |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D 638 |
MRC Polymers NAXALOYâ„¢ 770-NT137 ABS + PC Alloy Information provided by MRC Polymers Inc. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D 638 |
MRC Polymers NAXALOYâ„¢ 770-NT172 ABS + PC Alloy Information provided by MRC Polymers Inc. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KL003LH Acetal LNP* LUBRICOMP* KL003LH is an Acetal based compound containing 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WL002 PBT LNP* LUBRICOMP WL002 is a compound based on PBT resin containing 10% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON KS302 Acetal Copoly (Asia Pacific) LNP* Stat-kon* KS302 is a compound based on Acetal Copolymer resin containing Stainless Steel. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Europe-Africa-Middle East) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® LB-1010W PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HP-1011 PC/ABS, Unreinforced Material with superior flowability and small gas generation that can be used in the exterior material of mobile phonesInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 2 in/min; ASTM Test |
Styrolution Terluran® HH-106 ABS Terluran HH-106 is an injection molding ABS grade with high resistance to heat deformation and impact.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WX05505 PBT LNP* Thermocomp* WX05505 is a compound based on Thermoplastic Polyester (PBT) resin containing proprietary fillers. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX NX0031 PPE+PA NORYL GTX* NX0031 resin is a conductive resin specially designed for electrostatic painting and powder coating applications. This material combines high impact, good flow and conductivity. The mate.. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE) LNP* FP-EF-1004 is a fluoropolymer compound based on ETFE resin containing 20% Glass Fiber. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL PX2801Z PPE+HIPS (Asia Pacific) PPE+HIPS Unfilled FR V-0 100C |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
Videolar 585 Crystal Polystyrene (GPPS) High heat extrusion crystalSuperior oriented polystyrene sheetFeatures: Low melt flowHigh molecular weightApplications: Foam applications such as egg cartons, meat trays and food serviceSuperior ori.. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50mm/min; ISO 527-2, -1A |
Topas Advanced Polymers TOPAS® IT X1 Cyclic Olefin Copolymer (COC) TOPAS® IT X1 is an injection molding grade with heat and impact resistance. It is a moderately clear resin with high moisture barrier, chemical and heat resistance, making it suitable for products .. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
Wico Plast Wicoran 57 ABS, High Gloss ApplicationsInjection moldingCharacteristics:High glossAll information provided by Wico Plast, Warenhandelsges. mbH |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
Aclo Accucomp ABS ABS892BL High Heat Grade |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min |
Arkema Group Rilsan® AUM 50 NOIR T6LD Nylon 12, 50% Glass Bead Filled (Dry) Designation ISO 1874-PA12,MHLR,16-020,GB50Rigid grad with glass beads filler (50%) for injection molding. Available color: black. Reinforced light and heat stabilizing agents. Mold-release agent.Goo.. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527-1 |
Barlog Plastics KEBAFORM C 901 SO POM Copolymer unreinforced, improved wear and friction POMInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50mm/min; ISO 527 |
BASF Ultramid® 8350 HS BK-102 PA6 (Dry) Ultramid 8350 HS BK-102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness
combined with a.. |
|||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |