Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 5.60 MPa | 812 psi | ISO 527 |
Polimeri Europa Greenflex® MH 40 Ethylene Vinyl Acetate Copolymer - Injection Molding & Extrusion Greenflex MH 40 is an ethylene vinyl acetate copolymer (EVA) for injection molding and extrusion. Items produced with Greenflex MH 40 show high elasticity and good mechanical properties.Main Applic.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | -20% change after 70 hours @ 70°C; ASTM D412 |
Precision Polymer Engineering N40M Nitrile Rubber Nitrile Butadiene Rubber, 35-45 °IRHD. Medium acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet British Standard BS2751 BA40.Applications: Excellent resistance to petro.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | -20% change after 70 hours @ 100°C; ASTM D412 |
Precision Polymer Engineering N90L Nitrile Rubber Low Nitrile Rubber, 85-95 °IRHD. Low acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. ASTM designation = NBR. ISO designation = NBR. ASTM D2000 line call-out M6BG907, A14, B.. |
|||
Tensile Strength, Yield | 5.60 - 10.4 MPa | 812 - 1510 psi | ±30% change after 168 hours @ 70°C; ASTM D412 |
Precision Polymer Engineering R90B Natural Rubber Natural Rubber, 85-95 °IRHD. This material is based on high-quality plantation (Hevea) rubber, reinforced with carbon black.Applications: Natural rubber offers low compression set, high tensile st.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | ASTM D412 |
Precision Polymer Engineering S50A Silicone Rubber Blue Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent heat resistance and low temperature flexibility. Use.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | -20% change after 336 hours @ 200°C; ASTM D412 |
Precision Polymer Engineering S50D Silicone Rubber Black Silicone Rubber, 46-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated to meet UK Ministry of Defence Aircraft Materials Specificatio.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | ASTM D412 |
Precision Polymer Engineering S50G Silicone Rubber Green Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent heat resistance and low temperature flexibility. Us.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | ASTM D412 |
Precision Polymer Engineering S50Y Silicone Rubber Yellow Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent heat resistance and low temperature flexibility. U.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | M100 |
3M Dyneon™ Fluorel™ FG-5630Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. When compared to other food grade Dia.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | M100 |
3M Dyneon™ Fluorel™ FC-2145 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp.. |
|||
Tensile Strength, Yield | 5.60 MPa | 812 psi | Film Property, 50 µm thickness; ASTM D882 |
Arkema Group OREVAC® 9307 Y EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |