Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 400 MPa | 58000 psi | |
Niagara LaSalle 1117 Cold Finished Steel Bar This is a resulphurized steel with good machinability and surface finish, but not as good as the standard screw stocks. Its case hardening characteristics are superior and it develops an excellent c.. |
|||
Tensile Strength, Yield | 400 MPa @Temperature 760 °C |
58000 psi @Temperature 1400 °F |
|
Haynes Hastelloy® W alloy, gas metal arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
|
Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 %, Temperature 93.0 °C |
58000 psi @Strain 0.200 %, Temperature 199 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Tensile Strength, Yield | >= 400 MPa | >= 58000 psi | Minimum Guaranteed |
Industeel SOLEIL A2 13% Cr High Strength Martensitic Stainless Steel (QT550 Heat Treatment) Description: Soleil A2 has combined Chromium (~13%) and Carbon ~0.10%) additions to provide an excellent combination of high mechanical properties and improved corrosion resistance properties. The g.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
|
Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
|
Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Tensile Strength, Yield | >= 400 MPa | >= 58000 psi | After bake hardening |
SSAB Tunnplat Docol® 500DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is.. |
|||
Tensile Strength, Yield | 400 MPa | 58000 psi | |
ThyssenKrupp TBL Structural Steel This Material Specification applies to heavy plate with thicknesses up to 100 mm, made of the fine-grain structural steel TBL.Application: The steel may be used for welded constructions of different.. |
|||
Tensile Strength, Yield | 400 MPa | 58000 psi | |
Goodfellow Aluminum-Copper/SiC Metal Matrix Composite Information provided by Goodfellow. |
|||
Tensile Strength, Yield | 400 MPa | 58000 psi | 0° |
Hexcel® HexPly® ES70 120°C Curing Epoxy Matrix, Hybrid carbon/Aramid fabric 245 g/m2 Information provided by HexCel |
|||
Tensile Strength, Yield | 400 MPa @Temperature 23.0 °C |
58000 psi @Temperature 73.4 °F |
|
Hexcel® HexPly® F515 Epoxy Resin, 1581 Glass Fabric Hexcel designation: 1581-38"-F515; Fiber 150-1/2Information provided by HexCel |
|||
Tensile Strength, Yield | 400 MPa | 58000 psi | 0º |
Hexcel® HexPly® M34 75°C (167°F) Curing Epoxy Matrix, E-glass Balanced Fabric 600 g/m2 Information provided by HexCel |
|||
Tensile Strength, Yield | 400 MPa | 58000 psi | 90º, RT, Dry; EN2561 |
Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 52%/G1177 Glass/Carbon Fiber Information provided by HexCel |
|||
Tensile Strength, Yield | 400 - 483 MPa | 58000 - 70000 psi | 0.2% offset |
Eagle Brass 19210 XP-10 Copper Iron, Extra Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Tensile Strength, Yield | 400 - 483 MPa | 58000 - 70000 psi | 0.2% offset |
Eagle Brass 425 Tin Brass 2%, 3/4 Hard Alloy C425 is a low zinc-containing alloy with good combination of tensile strength, electrical conductivity, formability and corrosion resistance. Applications include electrical springs, connector.. |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 % |
>= 58000 psi @Strain 0.200 % |
|
CLAL-MSX ARCAP Anticorrosion AP1C H12 1/2 hard, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 % |
>= 58000 psi @Strain 0.200 % |
|
CLAL-MSX NICLAFOR® 1000 TD2 Quenched/Cold Rolled, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 % |
>= 58000 psi @Strain 0.200 % |
|
CLAL-MSX NICLAL 3444 H14 4/4 Hard Copper Alloy, diameter > 8 Copper Alloy, Free Cutting Bronze Main Characteristics: Excellent machineabilityHigh mechanical propertiesSelf lubricating alloyTypical Applications:Parts for connectorsFriction partsBearings-Pinions-Lock pinsInformation provided b.. |
|||
Tensile Strength, Yield | 400 MPa | 58000 psi | Typical |
Dura-Bar 80-55-06 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Tensile Strength, Yield | 400 - 555 MPa @Strain 0.200 % |
58000 - 80500 psi @Strain 0.200 % |
|
ALIMEX AMP 8000 Aluminum Plate AMP 8000 offers higher strength levels, good machinability and dimensional stability. Its tensile strength is up to 40% higher than AlZn5.5MgCu (7075). Moulding, (Prototypes) injection moulds, Jig .. |
|||
Tensile Strength, Yield | 400 - 485 MPa | 58000 - 70300 psi | |
ArcelorMittal FB 540 Hot rolled ferrite-bainite steel Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: FB 450, 540, 560 and 590. This family of steel.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
|
Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 %, Temperature 200 °C |
58000 psi @Strain 0.200 %, Temperature 392 °F |
|
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |