Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
PSM Industries PolyAlloys MIM-Fe-%3Si Grade 2 Soft Magnetic Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
Tensile Strength, Yield | 393 MPa @Diameter 12.7 mm |
57000 psi @Diameter 0.500 in |
|
Kaiser 6033 T6, T651 Rod & Bar Alloy 6033 is a higher strength version of alloy 6061, approaching properties typically obtainable with 2000 series alloys. The alloy was developed to also offer improved machinability over 6061. Th.. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Tensile Strength, Yield | 393 MPa @Diameter 12.7 mm |
57000 psi @Diameter 0.500 in |
|
Kaiser 4026 T651 Rod & Bar This alloy is used when high strength with wear and/or galling resistance is required. It can eliminate hard-coat anodizing in some applications. Typical applications include air compressor pistons .. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
HP Alloys Nitronic® 50 Austenitic Stainless, Annealed Annealed applies to tensile, impact, and hardness values and are for 3/4 in. diameter samples; other properties are typical of this alloy.Nitronic® 50 Stainless Steel provides a combination of co.. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
Universal Wire Works 2319 (AMS 4191) Aluminum Alloy Filler Metal Alloy 2319 is used on applications requiring good strength at high temperatures (600°F) and many cryogenic and aircraft parts. Primarily used where weld joints are capable of being heat treated to .. |
|||
Tensile Strength, Yield | 393 - 434 MPa | 57000 - 63000 psi | 0.2% offset |
Eagle Brass 151 ZHC® COPPER, Extra Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Tensile Strength, Yield | 393 - 476 MPa | 57000 - 69000 psi | 0.2% offset |
Eagle Brass 230 Red Brass, Hard CDA 230 is known for having an electrical conductivity of 37% IACS, red color, corrosion resistance, excellent formability and moderate strength. Typical uses include costume jewelry, eyelets, faste.. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
Carpenter Hiperco® 50 Fe-Co-V Soft Magnetic Alloy, 0.15 mm Strip Heat Treated 843°C Hiperco® alloy 50 is an iron-cobalt-vanadium soft magnetic alloy which exhibits high magnetic saturation (24 kilogauss), high D.C. maximum permeability, low D.C. coercive force, and low A.C. core l.. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 % |
57000 psi @Strain 0.200 % |
|
PSM Industries PolyAlloys MIM-Fe-%3Si Grade 1 Soft Magnetic Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
Tensile Strength, Yield | 393 MPa @Strain 0.200 %, Temperature 538 °C |
57000 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |