Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 34.8 MPa | 5050 psi | ASTM D638 |
RedEye On Demand PC/ABS for FDM Rapid Prototyping This thermoplastic polymer blend combines PC (Polycarbonate) and ABS (Acrylonitrile Butadiene Styrene) to produce an industrial material with a lot to offer. It combines the strength of PC with the .. |
|||
Tensile Strength, Yield | 34.8 - 119 MPa | 5050 - 17300 psi | Average value: 56.6 MPa Grade Count:724 |
Overview of materials for Polycarbonate/ABS Alloy, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Unreinforced". Each property range of values reported is minimum and maximum va.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 287ºF Cure Temperature MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 5 Minutes Milling MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CR030LN Polypropylene, Mini-Random Copolymer, Thermoforming COPYLENE™ CR030LN is a mini-random copolymer with a high performance nucleation system designed to yield high clarity thermoformed articles.Applications: ThermoformingInformation provided by Philli.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | ASTM D638 |
Washington Penn Homopolymer Polypropylene 10% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | ASTM D638 |
Washington Penn Homopolymer Polypropylene 20% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 287ºF Cure Temperature MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | 83% Ret. |
UBE UBESTA® 3030U Nylon 12 (After Sulfuric Acid (10%) for 500 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 5 Minutes Milling MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA TWP 502 Description: Transparent Weatherable PolymerInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 34.8 MPa | 5050 psi | 2 in/min; ASTM D638 |
Phillips 66 COPYLENE® CH008 Polypropylene, Homopolymer, Netting COPYLENE™ CH008 is a fractional melt flow polypropylene homopolymer resin available in pellet form. Applications: Raffia/Tapes/Strapping; Anti-Corrosion Coating; Geotextile & Agriculture; Nets. Rep.. |